UNE EN ISO 1183-1. ≥ 0,932. Density of. Geomembrane g/cm3. UNE EN ISO
1183-1. 0,946 ±. 0.004. UNE EN ISO 1133. D Condition (190ºC/2,16 Kg). ≤ 0,40.
1349-CPD-014 06 EN 13361, EN 13362, EN 13491, EN 13492, EN 13493
ATARFIL HDS Raw Material
High Density Polyethylene
ATARFIL HDS is a two-colour coextruded geomembrane manufactured from maximum quality high density polyethylene HDPE resins to which pigments with a UV stabilizer are added. As a result of its colour, the product obtains a high integration with environment, or enhance the superficial appearance of the geomembrane in ornamental applications. Available colours: Green, Blue, Turquoise, Ochre, Grey and White. Other colours under request for minimum orders, indicating RAL code. Thickness of coextruded layer can be modified. ATARFIL HDS contains 97.5% of pure polymer, and approximately 2.5% of Carbon Black, antioxidant, thermal stabilizers and signal layer in white colour. The product does not contain plasticizers of fillers that can migrate over time. Atarfil guarantees both UV resistance and colour stability for a variable time limit depending on the selected colour. The geomembrane ATARFIL HDS is manufactured under rigorous quality controls.
Surface
Colour
Smooth
Black + Colour Green 6001
RAL Code Unit
Test Method
Value
g/cm3
UNE EN ISO 1183-1
≥ 0,932
UNE EN ISO 1183-1
0,946 ± 0.004
3
g/cm
UNE EN ISO 1133 Melt Flow Index
g/10 min
Oxidative Induction Time (OIT) Stress Crack Resistance/NCTL
%
ASTM D 4218
2,0 - 2,5
min
UNE EN 728 (200ºC)
> 100
h
ASTM D 5397
≥ 400
%
UNE EN 14575
≤ 15
Oxidation
Tested Property
Test Method
mm
UNE EN 1849-2
Confidence level 95%
%
-
Confidence level 90%
%
-
Strength Characteristics Quality of Final Product
Tensile strength at Yield
Unit
Test Method
Value
-
UNE EN 495-5
No cracks
Water Permeability
m3/m2·día
UNE EN 14150
< 1·10 -6
Coefficient of Linear Thermal Expansion
1/ºC
ASTM D 696
2,15·10 -4
UNE EN ISO 62 (24h)
≤ 0,1
UNE EN ISO 62 (6 days)
≤ 0,1
%
UNE EN 1849-2
50
mm
ASTM D 7466
-
Water Absorption
Tensile strength at Break
Value 1.00
1.50
27 (24)
36 (32)
45 (40)
54 (48)
80 (65)
96 (78)
12 (9) 32 (26)
48 (39)
64 (52) 800 (700)
ISO 34-1
140 (135)
210 (202)
280 (270)
350 (337)
420 (405)
UNE-EN ISO 12236
3,0 (2.5)
4.5 (4.0)
5.5 (5.0)
6.5 (6.0)
6.8 (6.5)
N
Puncture Resistance
KN
Exploding Resistance
%
pr EN 14151
< 15
%
UNE EN ISO 14632 (100ºC, 1h)
± 1,5
PRESENTATION (Standard Sizes)
3.00
1
%
Tear Resistance
2.50
Tolerance: ± 4
UNE-EN ISO 527 (Type 5)
%
2.00 Tolerance: ± 6
18 (16)
N/mm
Elongation at Break
%
Thickness of Coextruded Layer
N/mm
Elongation at Yield
Parameter 181111
White 9016
Tensile Properties
Dimensional Stability
(*)
Grey 7040
Asperity Height
Unit
Thickness
(1)
≤ 1,30
T Condition (190ºC/5 Kg)
Carbon Black Content
Durability
UNE EN ISO 1133
Turquoise 5018
Low Temperature Brittleness (tª: -40ºC)
≤ 0,40
D Condition (190ºC/2,16 Kg)
Ochre 1001
Tested Property
Functional Properties
Raw Material Identification
Tested Property Density of Raw Material Density of Geomembrane
Blue 5012
Units
1,00
1,50
Roll width
m
6 / 6,30/ 7.50*
6 / 6,30/ 7.50*
Roll Length
m
210
140
105
84
70
840/882/1050
630/661/787
504/529/630
420/441/525
2
Surface 1260/1323/1575 m Values indicated are MEDIUM. In brackets values with 95% confidence level. Geomembrane manufactured in Dubai Plant.
2,00
2,50
3,00
6 / 6,30/ 7.50* 6 / 6,30/ 7.50* 6 / 6,30/ 7.50*
This information is provided for reference purposes and is not intended as guarantee. ATARFIL assumes no liability in connection with the use of this information or the final use of the product.