Composites of Graphene Quantum Dots and ... - ACS Publications

This is an open access article published under an ACS AuthorChoice License, which permits copying and redistribution of the article or any adaptations for non-commercial purposes.

Article Cite This: ACS Omega 2017, 2, 7293-7298

http://pubs.acs.org/journal/acsodf

Composites of Graphene Quantum Dots and Reduced Graphene Oxide as Catalysts for Nitroarene Reduction Jiali Zhang,† Fangwei Zhang,† Yaoyao Yang,† Shouwu Guo,*,† and Jingyan Zhang*,‡ †

Department of Electronic Engineering, School of Electronic Information and Electrical Engineering, Shanghai Jiao Tong University, Shanghai 200240, P. R. China ‡ State Key Laboratory of Bioreactor Engineering, Shanghai Key Laboratory of New Drug Design, School of Pharmacy, East China University of Science and Technology, Shanghai 200237, P. R. China S Supporting Information *

ABSTRACT: Composites of graphene quantum dots (GQDs) and reduced graphene oxide (rGO) with unique three-dimensional (3D) structure are prepared and their catalytic activities for reduction of nitroarenes are explored. We demonstrate that the 3D GQDs/rGO composites are more active in nitroarene reduction than GQDs and rGO. Some of them are even more active than the Ag-embedded calcium alginate (Ag/CA) or Au-embedded calcium alginate (Au/CA) catalysts. Interestingly, their catalytic property is closely related to the ratio of GQDs to rGO in the 3D GQDs/ rGO composites and GQDs-to-rGO mass ratio of 1/4 exhibits the highest catalytic activity. Raman spectra of the composites show that GQDs-to-rGO ratio is related to the number of the surface/edge defects, indicating that the sites of defect and edges are active sites. In addition, the catalytic performance of the 3D GQDs/rGO composites is also contributed by their unique 3D network structures that are beneficial for the reactant adsorption and product diffusion. Given also the long cycling duration and the easy recovery from the reaction system, 3D GQDs/rGO composites are potential applicable metal-free catalytic system for nitorarene reduction.

■

nitroarene reduction.24 Moreover, boron-doped onion-like carbon and carbon nanotubes (CNTs) also showed admirable catalytic activity and stability in nitroarene reduction.25 Recently, it was reported that the CNTs modified by H2O2 (oCNT) could catalyze nitroarene reduction, and it was proposed that the carbonyl groups in oCNT are of importance for their catalytic activity.26 However, exact catalytic mechanisms for most carbonaceous materials in nitroarene reduction remain unknown. Previously, our group and others discovered that the nanoarchitectures assembled with GQDs and other materials could significantly enhance the catalytic activity and stability of the metal catalysts owing to the excellent electron transportation capability and good chemical/physical stabilities of GQDs.27,28 For example, we have found that GQDs/Au system could efficiently catalyze the oxidation of aromatic alcohols because they were intimately absorbed on the catalyst.29 Additionally, as aforementioned, the surface/edge defects of GO and rGO sheets may determine their catalytic activities;18,22 thus, the hypothesis here is that the GQDs should have even larger periphery area than GO and rGO sheets. To this end, in this work, we designed and prepared composites of

INTRODUCTION Aromatic amines have been extensively used as intermediates or precursors for the syntheses of dyes, pigments, agrochemicals, pharmaceuticals, cosmetics, fibers, polymers, and photographic chemicals.1−3 Traditionally, aromatic amines have been obtained through the selective reductions of nitroarenes in the presence of various transition metals or precious metal catalysts.1,4 For instances, Pd,5 Au,6 Pt,7 Ru,8 Ag,9 Cu,10 Fe,11 Ni,12 and some bimetallics like AuAg,13 FePd,14 and PdCu15 have been successfully utilized. However, for most aforementioned noble metals, the high price and scarcity greatly limited their practical applications. Recently, metal-free catalysts, especially the nanostructured carbonaceous materials, have attracted great attention due to their high catalytic activities, low cost, environmental friendliness, and easy availability.16−21 For instance, reduced graphene oxide (rGO) was used in the hydrogenation of nitrobenzene at room temperature, and it was proposed that possibly the zigzag edges of rGO acted as catalytic active sites to facilitate the activation of a reactant molecule based on previous theoretic calculations.22 However, there is no quantitative method to define the number of edges or defect sites on rGO to support the hypothesis. Kong et al. reported that nitrogen-doped graphene (NG) could catalyze the reduction of 4-nitrophenol.23 Yang et al. also found that the graphitic NG exhibited the highest catalytic activity in the © 2017 American Chemical Society

Received: July 3, 2017 Accepted: September 19, 2017 Published: October 27, 2017 7293

DOI: 10.1021/acsomega.7b00908 ACS Omega 2017, 2, 7293−7298

ACS Omega

Article

interaction would become stronger when the GO sheets were reduced (rGO) during the hydrothermal treatment. It has been well documented that the hydrothermal treatment of the GO aqueous suspensions with appropriate concentration results in the formation of three-dimensional rGO (3D rGO).30 Figure 1a shows the scanning electron microscopy (SEM) image of the as-prepared GQDs/rGO4 composite (GQDs-to-GO ratio is 1:4 in weight), which displays a unique 3D network structure similar to the bare 3D rGO (Figure S2). Within the composite, the sheet motif of rGO was maintained well, and GQDs are anchored uniformly on the basal planes of 3D rGO, as shown in Figure 1b,c. The high-resolution transmission electron microscopy (HRTEM) illustrated that the interplane lattice constant of GQDs was around 0.2 nm, as shown in Figure 1d, which is very close to that of the graphite (0.213 nm), corresponding to the (101) facet.31,32 These results indicated clearly that GQDs/rGO composites with a unique 3D structure were prepared with a simple hydrothermal treatment of GQDs and GO. The reduction of the GO into 3D rGO in the composites was also confirmed by Fourier transform infrared (FT-IR) spectroscopy. As illustrated in Figure S3, the GO showed the vibration and deformation peaks of the −OH group at 3395 and 1410 cm−1, the stretching vibration peak of −CO group at 1730 cm−1 and the stretching vibration peak of −C−O group of epoxy and alkoxy at 1226 and 1052 cm−1, respectively.33 In the IR spectrum of 3D GQDs/rGO, peaks for −OH and −C− O group of epoxy and alkoxy disappeared, suggesting that GO was reduced. Catalytic Activities of the 3D GQDs/rGO Composites. The catalytic performance of the 3D GQDs/rGO composites in the reduction of nitroarene with NaBH4 as a reducing agent was first elaborated using 4-nitrophenol as a model compound, and the reduction process was monitored with UV−vis spectroscopy. As shown in Figure 2a, there are three UV−vis absorption peaks for 4-nitrophenol in the 200−500 nm range,

GQDs and hydrothermally reduced graphene oxide (GQDs/ rGO), and explored their catalytic activity in nitroarene reduction. As will be shown, the GQDs/rGO composites assume a unique three-dimensional (3D) structure with rGO sheets as structural (networks) matrices, and GQDs are anchored on them; under moderate conditions, the reduction of nitroarene can be preceded with 3D GQDs/rGO composites as catalysts, and the composites exhibited overall higher catalytic activity than individual GQDs and rGO.

■

RESULTS AND DISCUSSION Preparations and Characterizations of 3D GQDs/rGO Composites. The morphologies of raw GO and GQDs used in the work were characterized by atomic force microscopy (AFM) (Figure S1). The average lateral size of GO sheets reached to a few micrometers, and the average lateral size of GQDs was ∼10 nm. GO and GQDs assumed the same planar aromatic carbon backbone structure; therefore, as illustrated in Scheme 1, when GQDs and GO aqueous suspensions were Scheme 1. Illustration of the Formation Process of the 3D GQDs/rGO Composites

mixed, GQDs would attach to the basal plane of GO through strong π−π stacking, and the intensity of such kind of

Figure 1. SEM (a), TEM (b, c), and HRTEM (d) images of the 3D GQDs/rGO4 composite. 7294


ACS Omega

Article

Figure 2. (a) UV−vis spectra of the reduction of 4-nitrophenol catalyzed by 3D GQDs/rGO4 at RT, the time interval is 2 min. (b) Time courses of the 4-nitrophenol reduction using GQDs, 3D rGO, GQDs/rGO1, GQDs/rGO2, GQDs/rGO4, and GQDs/rGO6 composites as catalysts monitored at 400 nm. Reaction condition: 0.048 mg catalyst, 0.5 μmol substrate, and molar ratio of 4-nitrophenol to NaBH4 is 1:53.

GQDs/rGO4, and 3D GQDs/rGO6 were 1.039, 1.234, 1.270, 1.317, 1.322, and 1.287, respectively. The increasing ID/IG values from GQDs, to 3D rGO, and to GQDs/rGO composites confirmed that the incorporation of GQDs to rGO led to the generation of more surface/edge defects. Among them, 3D GQDs/rGO4 composite has the highest ID/IG value, implying that it contained more surface/edge defects than the others. That should be the main reason why the 3D GQDs/rGO4 has an overall better catalytic performance than bare GQDs, 3D rGO, and other as-studied composites. The kinetics of the reductions of nitroarenes using 3D GQDs/rGO composites with different GQDs-to-rGO ratios as catalysts was monitored by measuring the UV−vis absorption intensity variation at 400 nm (Figure 2b). Figure S6 shows the linear correlations of c−c0 (c and c0 represent the concentrations of 4-nitrophenol at reaction times of t and 0, respectively) versus time for the different catalysts.4,35,36 Accordingly, the rate constant (k) were obtained from the slope of the curves of c−c0 versus t and are listed in Table 1. The reaction rate constants with 3D GQDs/rGO composites as catalysts generally increased with decrease in the GQDs-to-rGO ratio, but reached the maximum when the GQDs-to-rGO ratio is 1:4, revealing that the 3D GQDs/rGO4 has the highest catalytic activity in the reduction of 4-nitrophenol. This is consistent with the Raman spectroscopic results (3D GQDs/ rGO4 assume largest ID/IG values; Figure 3). It is also worth pointing out that all of the composites assumed generally higher catalytic activity than individual 3D rGO or GQDs. The catalyst turnover frequency (TOF), the number of nitroarene molecules that were reduced using 1 g of catalyst per second, was also calculated (Table 1). TOF of the 3D GQDs/rGO is generally much higher than that of Ag/CA and Au/CA.36 It was reported that Au nanoparticles decorated on thiol-functionalized reduced graphene oxide (Au/SRG) was a very efficient catalyst for nitroarene reduction.37 However, no data of the SRG alone were reported; it is not easy to conclude the role of SRG in the Au/SRG composite by comparing the polygonal Au nanoparticles that are in a total different state with the Au modified by SRG. Given that other conditions are the same, the only difference between the composites are the number of GQDs on the basal plane of rGO; we thus conclude that the surface/edge defects within 3D GQDs/rGO act as the active sites. Actually, similar results was observed with native and H2O2-treated carbon nanotubes CNTs as catalysts, the latter being more active.26 It was also reported recently that GQDs

the intensity of the peak at 400 nm decreased rapidly with the progress in reduction and disappeared after 10 min of reaction. Meanwhile, the appearance of a new absorption peak at 300 nm originating from 4-aminophenol indicated the reduction of 4nitrophenol to 4-aminophenol.23,34 In contrast, NaBH4 is not able to reduce 4-nitrophenol without a catalyst under the same conditions (Figure S4). The reaction was further evaluated using high-performance liquid chromatography (HPLC) and ultraperformance liquid chromatography quadrupole time-offlight mass spectrometer (UPLC-Q-TOF-MS) (Figure S5). Only one peak with a retention time of 2.838 min corresponding to the product 4-aminophenol was detected (Figure S5b,c). The results imply that 4-nitrophenol can be reduced by NaBH4 with 3D GQDs/rGO composite as a catalyst at room temperature. Surface/Edge Defects of the 3D GQDs/rGO Composites Determine Their Catalytic Activities. It was proposed in early works that the surface/edge defects of the rGO might be the catalytic active sites.18,22 To illustrate the assumption, the Raman spectra of 3D GQDs/rGO composites with different GQDs-to-rGO ratios were collected and are shown in Figure 3. In principle, the intensity ratios of D and G bands in Raman spectra (ID/IG) of 3D GQDs/rGO composites reflect the amounts of the surface/edge defects of the GQDs and rGO sheets. Actually, as shown in Figure 3, the ID/IG values of GQDs, 3D rGO, 3D GQDs/rGO1, 3D GQDs/rGO2, 3D

Figure 3. Raman spectra of GQDs (a), 3D rGO (b), 3D GQDs/rGO1 (c), 3D GQDs/rGO2 (d), 3D GQDs/rGO4 (e), and 3D GQDs/rGO6 (f). 7295


ACS Omega

Article

Table 1. Rate Constants and TOF of the Reduction of 4-Nitrophenol with Different Catalysts entry 1 2 3 4 5 6 7 8 9 10

catalyst

k (×10−7 M s−1)

TOF (×1019 molecules g−1 s−1)

2.21 2.27 3.28 3.65 4.47 3.04 1.72−1.73 0.23−0.33 0.73 83.3

0.96 1.04 1.42 1.57 1.69 1.28 0.0093 0.0017

a

GQDs 3D rGOa 3D GQDs/rGO1a 3D GQDs/rGO2a 3D GQDs/rGO4a 3D GQDs/rGO6a Ag/CAb Au/CAb nonec Ag/SRGd

ref this this this this this this 36 36 23 37

work work work work work work

a Reaction conditions: 0.048 mg of GQDs, 3D rGO, or 3D GQDs/rGO, 0.5 μmol substrate, molar ratio of nitroarene to NaBH4 is 1:53, RT. Conversions of nitroarenes and yields of amine were determined by HPLC using external standard method. bReaction conditions: 1.2 g L−1 catalyst, 0.1 M NaBH4, 6−14 ×10−5 M 4-nitrophenol. cReaction conditions: 0.137 mg of catalyst, 0.5 μmol substrate, molar ratio of 4-nitrophenol to NaBH4 is 1:100, room temperature. dReaction conditions: 20 mg of catalyst, 20 μmol 4-nitrophenol, 0.8 mmol NaBH4.

Table 2. Catalytic Activity of the 3D GQDs/rGO4 in the Reduction of Various Nitroarenesa entry

substrate

product

t (min)

k (×10−7 M−1 s−1)

conversion (%)

yield (%)

1 2 3 4 5 6

4-nitrophenol 4-nitrotoluene 4-nitroanisole 4-nitrochlorobenzene 2-nitroanline 1,3-dinitrobenzene

4-aminophenol 4-aminotoluene p-anisidine 4-chloroaniline 1,2-diaminobenzene 1,3-diaminobenzene

10 9 12 18 15 15

4.47 4.48 3.38 1.95 1.74 1.26

>99 >99 >99 >99 >99 >99

92.93 85.73 84.22 51.67 66.68 46.60

Reaction conditions: 0.048 mg of 3D GQDs/rGO4, 0.5 μmol substrate, molar ratio of nitroarene and NaBH4 is 1:53, RT. Conversions of nitroarenes and yields of amine were determined by HPLC using external standard method. a

and graphene nanoribbons (GNRs) composites exhibited ultrahigh electrocatalytic performance for oxygen reduction and were proposed through numerous surface/edge defects in GQD/GNR to act as active sites.38 The high catalytic activity of 3D GQDs/rGO might also be contributed by their unique 3D morphologies. The catalytic activity of chemically reduced GO33 was much lower than that of 3D rGO we used in this work (Figure S7a,b). The adsorption of reactants on the surface of GO has been identified as one of critical steps for their catalysis.23,24 It is possible that the 3D network structural feature is helpful for the substrate adsorption as well as product diffusion. However, the specific surface area of 3D GQDs/rGO (∼178 m2 g−1) determined by nitrogen adsorption/desorption isotherm curves is lower than that of rGO (∼220 m2 g−1), and the surface area of 3D GQDs/rGO is quite similar to that of 3D rGO (Figure S8). The difference between the surface areas of rGO and 3D rGO is not unexpected because of their different preparation methods, as described in Experimental Section. In addition, the result further confirms that the catalytic activity of 3D GQDs/ rGO is primarily determined by the surface/edge defects within the composites. Taken together, the surface/edge defects combined with the unique 3D structure of 3D GQDs/rGO composites made them active catalysts for nitroarene reduction. Catalytic Activity of 3D GQDs/rGO in the Reduction of Nitroarene Derivatives. The catalytic activity of the 3D GQDs/rGO composites was also tested for the reductions of 4nitrotoluene, 4-nitroanisole, 4-nitrochlorobenzene, 2-nitroanline, and 1,3-dinitrobenzene under the same reaction conditions, and the results are shown in Figure S9, S10, and Table 2. Generally, all of the derivatives of nitroarene examined could be reduced with 3D GQDs/rGO as a catalyst. As shown in Table 2, the reduction of the nitroarenes containing electron-

withdrawing groups was much slower than that of those containing electron-donating groups. It means that electrondonating groups on the aromatic ring do favor for the reduction of nitroarenes. For instance, the reduction yield of 4nitrophenol is 92.93% (entry 1), whereas the reduction of 4nitrochlorobenzene was only about 51.67% (entry 4). The lower reduction yield was due to the formation of byproducts, as confirmed by UPLC-Q-TOF-MS (Figure S11). The fast rates and high yields indicated that the 3D GQDs/rGO was an efficient catalyst for the reduction of nitroarenes containing the electron-donating groups, such as −OH, −CH3, and −OCH3. Through detecting the reduction intermediates of different substrates (Figure S12), we found that nitrosobenzene and hydroxylamine were detected in the reduction of 4-aminophenol after 3 min of reaction (in the middle of the reaction; Figure 2a), whereas hydroxylamine, azobenzene, and hydrazobenzene were found in the reduction of 4-nitrotoluene. These different intermediates implied that the reduction pathway for nitroarenes with 3D GQDs/rGO as a catalyst might be closely related to the substrates. When substrate nitroarenes contain stronger electron-donating groups (like −OH) on its aromatic ring, reduction seems a direct pathway; if weaker electrondonating groups (like −CH3) is on the aromatic ring, the condensation pathway is more likely.39,40 For practical application, the stability of the 3D GQDs/rGO composites during catalytic reaction was tested. The composites were separated from the reaction system through centrifugation and washed three times with methanol and reused. As shown in Figure S13, no obvious deactivation was detected after 10 successive runs. In addition, the SEM image of the sample after the catalytic cycles shows that the composite retain the three-dimensional network (Figure S14), suggesting that 3D GQDs/rGO composites have a good reusability and 7296


ACS Omega

Article

SEM images were acquired using Ultra 55 field emission scanning electron microscope (Zeiss, Germany) with the working voltage of 10.0 kV. the TEM images were obtained on a JEOL JEM-2100F transmission electron microscope (JEOL, Japan) with the operation voltage of 200 kV. The highresolution TEM (HRTEM) images were recorded on the same instrument. The TEM specimens were prepared by placing the ethanol suspensions on the copper grids and drying under ambient condition. The FT-IR spectra were acquired on a EQUINOX 55 FT-IR spectrometer (Bruker, Germany). The specimens for FT-IR measurement were prepared by grinding the dried powder of GO, rGO, or GQDs/rGO with KBr together and then compressing it into thin pellets. Raman measurements were performed on a Senterra R200-L Dispersive Raman Microscope (Bruker, Germany) with the excitation laser beam wavelength of 633 nm. The powders of GQDs, rGO, and GQDs/rGO after grinding were used for the Raman measurement. The surface area was determined using the Brunauer−Emmett−Teller (BET) method by ASAP 2020 M (Micromeritics). Catalytic reactions were monitored using a UV-2550 UV−vis spectrometer (Shimadzu, Japan). After the reaction, the conversion of nitroarene and yield of corresponding aniline were analyzed by 1220 HPLC (Agilent Technologies) with phosphate buffer (A) and acetonitrile (B) as mobile phase. The reaction mixture and reaction intermediates were analyzed by ACQUITY UPLC & Q-TOF MS Premier (Waters) with water (A) and acetonitrile (B) as mobile phase under gradient elution conditions.

stability that should be practically applicable in the reduction of nitroarenes.

■

CONCLUSIONS Three-dimensional GQDs/rGO composites with different ratios of GQDs versus GO were prepared via one-pot hydrothermal method. The 3D GQDs/rGO composites showed improved catalytic activities for the reduction of nitroarene compared with GQDs, 3D rGO, and some metal catalysts. The high catalytic activity of the 3D GQDs/rGO is directly related to the GQDs-to-rGO ratio, which reflects the content of surface/edge defects within the composites. The catalytic activities of the 3D GQDs/rGO composites are also contributed by their unique structures. The unique 3D structure seems helpful for the absorption of reactants on the surface of 3D GQDs/rGO composites and prompts the product diffusion in the catalyst. It was also found that the 3D GQDs/rGO composites have higher catalytic activities for the nitroarenes with electron-donating groups on their aromatic rings. This, coupled with their high stability and ease of separation and recyclability, indicated that 3D GQDs/rGO could find practical applications in the reductions of nitroarenes.

■

EXPERIMENTAL SECTION Materials. 4-Nitrophenol, 4-nitrotoluene, 4-nitroanisole, 4nitrochlorobenzene, 2-nitroanline, 1,3-dinitrobenzene, and sodium borohydride (NaBH4) were purchased from Sinopharm Chemical Reagent Co., Ltd., Shanghai, China. All of the chemicals were used as received. GO and GQDs were prepared following the procedures described in our previous works.33,41 Preparation of 3D GQDs/rGO Composites. In a typical experiment, 12 mL, 2 mg/mL aqueous dispersion of GO was added to an 30 mL autoclave, GQDs were then added to get final GQDs/GO ratios of 1:1, 1:2, 1:4, and 1:6 (in weight) and stirred for 10 min. The autoclaves were transferred to an oven and kept at 180 °C for 9 h. During the thermal treatment, GO was reduced and abbreviated as 3D rGO. After cooling down to room temperature, the solid products were separated through centrifuging and washing three times with deionized water. Finally, the composites were dried for 24 h in a vacuum freezing-dryer. The corresponding composites are named as 3D GQDs/rGO1, GQDs/rGO2, GQDs/rGO4, and GQDs/rGO6 corresponding to their initial GQDs-to-GO ratios of 1:1, 1:2, 1:4, and 1:6 (in weight). For comparison, 3D rGO was prepared by hydrothermal reaction of the GO without GQDs under similar condition. Catalytic Reduction of Nitroarene. Nitroarene (0.5 mL, 1 mM), NaBH4 (2 mL, 5 mg/10 mL), and 3D GQDs/rGO (48 μL, 1 mg/mL) were mixed in a UV−vis cuvette. The reduction reaction was followed by monitoring UV−vis absorption of the reaction mixture at λmax at room temperature. The reduction reactions of nitroarene were also conducted with bare rGO and GQDs as catalysts under the same condition as controls. Instrumental. Atomic force microscopic (AFM) images of GQDs and GO were taken on a MultiMode Nanoscope V scanning probe microscopy system (Veeco), and AN-NSC 10AFM cantilever tips (SHNIT Co., Russia) with a force constant of ∼37 N/m and resonance vibration frequency of ∼330 kHz were used. Samples for AFM were prepared by dropping the aqueous suspension (∼0.02 mg/mL) of GO or GQDs on a freshly cleaved mica surface and dried in air. The

■

ASSOCIATED CONTENT

S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsomega.7b00908. Characterization data for GO, GQDs, rGO, 3D rGO, and 3D GQDs/rGO composites and detailed data regarding catalytic experiments (PDF)

■

AUTHOR INFORMATION

Corresponding Authors

*E-mail: [email protected]. Tel/Fax: 0086-21-34206915 (S.G.). *E-mail: [email protected]. Tel/Fax: 0086-21-64253846 (J.Z.). ORCID

Shouwu Guo: 0000-0002-2219-7700 Jingyan Zhang: 0000-0001-6979-0969 Author Contributions

The manuscript was written through contributions of all of the authors. All of the authors have given approval to the final version of the manuscript. Notes

The authors declare no competing financial interest.

■

ACKNOWLEDGMENTS The work was financially supported by the National “973 Program” of China (No. 2015CB931801), the National Natural Science foundation of China (Nos. 11374205 and 21376148).

■

REFERENCES

(1) Downing, R. S.; Kunkeler, P. J.; Bekkum, H. v. Catalytic Syntheses of Aromatic Amines. Catal. Today 1997, 37, 121−136.

7297


ACS Omega

Article

(22) Gao, Y.; Ma, D.; Wang, C.; Guan, J.; Bao, X. Reduced Graphene Oxide as a Catalyst for Hydrogenation of Nitrobenzene at Room Temperature. Chem. Commun. 2011, 47, 2432−2434. (23) Kong, X.-k.; Sun, Z.-y.; Chen, M.; Chen, C.-l.; Chen, Q.-w. Metal-Free Catalytic Reduction of 4-Nitrophenol to 4-Aminophenol by N-Doped Graphene. Energy Environ. Sci. 2013, 6, 3260−3266. (24) Yang, F.; Chi, C.; Wang, C.; Wang, Y.; Li, Y. High Graphite N Content in Nitrogen-Doped Graphene as an Efficient Metal-Free Catalyst for Reduction of Nitroarenes in Water. Green Chem. 2016, 18, 4254−4262. (25) Lin, Y.; Wu, S.; Shi, W.; Zhang, B.; Wang, J.; Kim, Y. A.; Endo, M.; Su, D. S. Efficient and Highly Selective Boron-Doped Carbon Materials-Catalyzed Reduction of Nitroarenes. Chem. Commun. 2015, 51, 13086−13089. (26) Wu, S.; Wen, G.; Schlogl, R.; Su, D. S. Carbon Nanotubes Oxidized by a Green Method as Efficient Metal-Free Catalysts for Nitroarene Reduction. Phys. Chem. Chem. Phys. 2015, 17, 1567−1571. (27) Pan, D.; Xi, C.; Li, Z.; Wang, L.; Chen, Z.; Lu, B.; Wu, M. Electrophoretic Fabrication of Highly Robust, Efficient, and Benign Heterojunction Photoelectrocatalysts Based on Graphene-QuantumDot Sensitized Tio2 Nanotube Arrays. J. Mater. Chem. A 2013, 1, 3551−3555. (28) Zhou, X.; Tian, Z.; Li, J.; Ruan, H.; Ma, Y.; Yang, Z.; Qu, Y. Synergistically Enhanced Activity of Graphene Quantum Dot/MultiWalled Carbon Nanotube Composites as Metal-Free Catalysts for Oxygen Reduction Reaction. Nanoscale 2014, 6, 2603−2607. (29) Wu, X.; Guo, S.; Zhang, J. Selective Oxidation of Veratryl Alcohol with Composites of Au Nanoparticles and Graphene Quantum Dots as Catalysts. Chem. Commun. 2015, 51, 6318−6321. (30) Xu, Y.; Sheng, K.; Li, C.; Shi, G. Self-Assembled Graphene Hydrogel Via a One-Step Hydrothermal Process. ACS Nano 2010, 4, 4324−4330. (31) Pan, D.; et al. Cutting Sp2 Clusters in Graphene Sheets into Colloidal Graphene Quantum Dots with Strong Green Fluorescence. J. Mater. Chem. 2012, 22, 3314−3318. (32) Du, F.; et al. Nitrogen-Doped Carbon Dots with Heterogeneous Multi-Layered Structures. RSC Adv. 2014, 4, 37536−37541. (33) Zhang, J.; Yang, H.; Shen, G.; Cheng, P.; Zhang, J.; Guo, S. Reduction of Graphene Oxide Via L-Ascorbic Acid. Chem. Commun. 2010, 46, 1112−1114. (34) Wunder, S.; Polzer, F.; Lu, Y.; Mei, Y.; Ballauff, M. Kinetic Analysis of Catalytic Reduction of 4-Nitrophenol by Metallic Nanoparticles Immobilized in Spherical Polyelectrolyte Brushes. J. Phys. Chem. C 2010, 114, 8814−8820. (35) Pradhan, N.; Pal, A.; Pal, T. Catalytic Reduction of Aromatic Nitro Compounds by Coinage Metal Nanoparticles. Langmuir 2001, 17, 1800−1802. (36) Saha, S.; Pal, A.; Kundu, S.; Basu, S.; Pal, T. Photochemical Green Synthesis of Calcium-Alginate-Stabilized Ag and Au Nanoparticles and Their Catalytic Application to 4-Nitrophenol Reduction. Langmuir 2010, 26, 2885−2893. (37) Liu, W.; Sun, D.; Fu, J.; Yuan, R.; Li, Z. Assembly of Evenly Distributed Au Nanoparticles on Thiolated Reduced Graphene Oxide as an Active and Robust Catalyst for Hydrogenation of 4-Nitroarenes. RSC Adv. 2014, 4, 11003−11011. (38) Jin, H.; Huang, H.; He, Y.; Feng, X.; Wang, S.; Dai, L.; Wang, J. Graphene Quantum Dots Supported by Graphene Nanoribbons with Ultrahigh Electrocatalytic Performance for Oxygen Reduction. J. Am. Chem. Soc. 2015, 137, 7588−7591. (39) Corma, A.; Concepcion, P.; Serna, P. A Different Reaction Pathway for the Reduction of Aromatic Nitro Compounds on Gold Catalysts. Angew. Chem., Int. Ed. 2007, 46, 7266−7269. (40) Wu, S.; Wen, G.; Zhong, B.; Zhang, B.; Gu, X.; Wang, N.; Su, D. Reduction of Nitrobenzene Catalyzed by Carbon Materials. Chin. J. Catal. 2014, 35, 914−921. (41) Zhou, X.; Zhang, Y.; Wang, C.; Wu, X.; Yang, Y.; Zheng, B.; Wu, H.; Guo, S.; Zhang, J. Photo-Fenton Reaction of Graphene Oxide: A New Strategy to Prepare Graphene Quantum Dots for DNA Cleavage. ACS Nano 2012, 6, 6592−6599.

(2) Nomura, K. Transition Metal Catalyzed Hydrogenation or Reduction in Water. J. Mol. Catal. A: Chem. 1998, 130, 1−28. (3) Wegener, G.; et al. Trends in Industrial Catalysis in the Polyurethane Industry. Appl. Catal., A 2001, 221, 303−335. (4) Begum, R.; Rehan, R.; Farooqi, Z. H.; Butt, Z.; Ashraf, S. Physical Chemistry of Catalytic Reduction of Nitroarenes Using Various Nanocatalytic Systems: Past, Present, and Future. J. Nanopart. Res. 2016, 18, 231. (5) Mei, Y.; Lu, Y.; Polzer, F.; Ballauff, M. Catalytic Activity of Palladium Nanoparticles Encapsulated in Spherical Polyelectrolyte Brushes and Core-Shell Microgels. Chem. Mater. 2007, 19, 1062− 1069. (6) Lee, J.; Park, J. C.; Bang, J. U.; Song, H. Precise Tuning of Porosity and Surface Functionality in Au@Sio2 Nanoreactors for High Catalytic Efficiency. Chem. Mater. 2008, 20, 5839−5844. (7) Zou, P.; Wang, M.; Zhao, L.; Dai, L.; Wang, Y. One-Step Synthesis of Pt@Three-Dimensional Graphene Composite Hydrogel: An Efficient Recyclable Catalyst for Reduction of 4-Nitrophenol. Appl. Organomet. Chem. 2016, 30, 722−725. (8) Gopiraman, M.; Babu, S. G.; Khatri, Z.; Wei, K.; Endo, M.; Karvembu, R.; Kim, I. S. Facile and Homogeneous Decoration of Ruo2 Nanorods on Graphene Nanoplatelets for Transfer Hydrogenation of Carbonyl Compounds. Catal. Sci. Technol. 2013, 3, 1485−1489. (9) Pradhan, N.; Pal, A.; Pal, T. Silver Nanoparticle Catalyzed Reduction of Aromatic Nitro Compounds. Colloids Surf., A 2002, 196, 247−257. (10) Kaur, R.; Pal, B. Cu Nanostructures of Various Shapes and Sizes as Superior Catalysts for Nitro-Aromatic Reduction and Co-Catalyst for Cu/Tio2 Photocatalysis. Appl. Catal., A 2015, 491, 28−36. (11) Jagadeesh, R. V.; Surkus, A.-E.; Junge, H.; Pohl, M.-M.; Radnik, J.; Rabeah, J.; Huan, H.; Schünemann, V.; Brückner, A.; Beller, M. Nanoscale Fe2o3-Based Catalysts for Selective Hydrogenation of Nitroarenes to Anilines. Science 2013, 342, 1073−1076. (12) Marakatti, V. S.; Peter, S. C. Nickel−Antimony Nanoparticles Confined in Sba-15 as Highly Efficient Catalysts for the Hydrogenation of Nitroarenes. New J. Chem. 2016, 40, 5448−5457. (13) Wu, T.; Zhang, L.; Gao, J.; Liu, Y.; Gao, C.; Yan, J. Fabrication of Graphene Oxide Decorated with Au−Ag Alloy Nanoparticles and Its Superior Catalytic Performance for the Reduction of 4-Nitrophenol. J. Mater. Chem. A 2013, 1, 7384−7390. (14) Metin, Ö ; Mendoza-Garcia, A.; Dalmızrak, D.; Gültekina, M. S.; Sun, S. FePd Alloy Nanoparticles Assembled on Reduced Graphene Oxide as a Catalyst for Selective Transfer Hydrogenation of Nitroarenes to Anilines Using Ammonia Borane as a Hydrogen Source. Catal. Sci. Technol. 2016, 6, 6137−6143. (15) Feng, Y.-S.; Ma, J.-J.; Kang, Y.-M.; Xu, H.-J. Pdcu Nanoparticles Supported on Graphene: An Efficient and Recyclable Catalyst for Reduction of Nitroarenes. Tetrahedron 2014, 70, 6100−6105. (16) Zhang, J.; Liu, X.; Blume, R.; Zhang, A.; Schlogl, R.; Su, D. S. Surface-Modified Carbon Nanotubes Catalyze Oxidative Dehydrogenation of N-Butane. Science 2008, 322, 73−77. (17) Dreyer, D. R.; Jia, H. P.; Bielawski, C. W. Graphene Oxide: A Convenient Carbocatalyst for Facilitating Oxidation and Hydration Reactions. Angew. Chem., Int. Ed. 2010, 49, 6813−6816. (18) Navalon, S.; Dhakshinamoorthy, A.; Alvaro, M.; Garcia, H. Carbocatalysis by Graphene-Based Materials. Chem. Rev. 2014, 114, 6179−212. (19) Yang, Z.; Yao, Z.; Li, G.; Fang, G.; Nie, H.; Liu, Z.; Zhou, X.; Chen, X.; Huang, S. Sulfur-Doped Graphene as an Efficient Metal-Free Cathode Catalyst for Oxygen Reduction. ACS Nano 2012, 6, 205−211. (20) Yao, Z.; Nie, H.; Yang, Z.; Zhou, X.; Liu, Z.; Huang, S. CatalystFree Synthesis of Iodine-Doped Graphene Via a Facile Thermal Annealing Process and Its Use for Electrocatalytic Oxygen Reduction in an Alkaline Medium. Chem. Commun. 2012, 48, 1027−1029. (21) Yang, Z.; Nie, H.; Chen, X. a.; Chen, X.; Huang, S. Recent Progress in Doped Carbon Nanomaterials as Effective Cathode Catalysts for Fuel Cell Oxygen Reduction Reaction. J. Power Sources 2013, 236, 238−249. 7298