Catalysis Science & Technology PAPER

10 downloads 0 Views 3MB Size Report
addition of NaOH for dimethyl carbonate synthesis.15 The ..... Table 2 Cross-aldol condensation reaction of aromatic aldehydes with cyclohexanonea. No.
Catalysis Science & Technology

Dynamic Article Links

Cite this: Catal. Sci. Technol., 2011, 1, 1653–1664

PAPER

www.rsc.org/catalysis

Synthesis and characterization of versatile MgO–ZrO2 mixed metal oxide nanoparticles and their applicationsw Manoj B. Gawande,*a Paula S. Branco,a Kalpesh Parghi,b Janhavi J. Shrikhande,b Rajesh Kumar Pandey,c C. A. A. Ghumman,d N. Bundaleski,d O. M. N. D. Teodorod and Radha V. Jayaramb Received 9th July 2011, Accepted 4th October 2011 DOI: 10.1039/c1cy00259g A heterogeneous, versatile nano-magnesia-zirconia or MgO–ZrO2 (MZ) catalyst was prepared by an ultra dilution method. The as-synthesised catalyst was characterized by several analytical techniques such as XRD, particle size analysis, BET surface area, thermogravimetric analysis (TGA), differential thermal analysis (DTA), FT-IR spectroscopy, SEM (scanning electron microscope), TEM (transmission electron microscope) and XPS (X-ray fluorescence spectroscopy). The surface area is found to be 268 m2 g1. The catalytic activity of MZ was tested for various important organic reactions such as cross-aldol condensation, N-benzyloxycarbonylation of amines, reduction of aromatic nitrocompounds, and synthesis of 1,5-benzodiazepines. It has been observed that for all reactions MZ shows a good catalytic activity. All corresponding products were obtained in good to excellent yield under mild conditions. The MgO-ZrO2 catalyst can be prepared from inexpensive precursors, has high surface area, and is reusable and recyclable for all reactions.

Introduction In heterogeneous catalysis, mixed metal oxides (MMOs) play a very important role because of their versatile chemical and physical properties and wide applications in the field of catalysis and technology.1–5 Mixed metal oxides represent one of the most important and widely employed classes of solid catalysts, either as active phases or supports. Mixed oxides are applied both for their acid–base and redox properties and constitute the largest family of catalysts in heterogeneous catalysis.6 There is very much interest to understand the phenomena for the deposition of one oxide on another oxide. There are various methods for the preparation of MMOs such as

a

REQUIMTE, Department of Chemistry, Faculty of Science and Technology, New University of Lisbon, Quinta da Torre, 2829-516 Caparica, Lisbon, Portugal. E-mail: [email protected], [email protected]; Fax: +351 21 2948550; Tel: +351 96 4223243, +351 21 2948300 b Department of Chemistry, Institute of Chemical Technology, Nathalal Parekh Marg, Matunga, Mumbai, India. E-mail: [email protected] c Department of Chemistry, Marquette University, Milwaukee, WI-53233, USA d Centre for Physics and Technological Research (CeFITec), Departamento de Fı´sica da Faculdade de Cieˆncias e Tecnologia (FCT), Universidade Nova de Lisboa, 2829–516 Caparica, Portugal w Electronic supplementary information (ESI) available: See DOI: 10.1039/c1cy00259g

This journal is

c

The Royal Society of Chemistry 2011

sol–gel,7 wet impregnation,8 mechanochemical synthesis,9 hydrothermal method,10 and co-precipitation.11 Recently Parida et al prepared nano-sized iron–cerium mixed oxides with diameters ranging from 10 to 20 nm by slow addition of a precipitating agent and reported their application as photocatalysts for dye degradation.12 Nanometer coupled oxide ZnO–SnO2 was prepared by An et al using the co-precipitation method, with slow addition of aqueous ammonia.13 Zhang and co-workers prepared nanosized ZnO–SnO2 with high photocatalytic activity by slow addition of NaOH as a precipitating agent with vigorous stirring.14 Yoo and coworkers synthesized MgO–CeO2 mixed oxide catalysts by co-precipitation using ionic liquid and slow addition of NaOH for dimethyl carbonate synthesis.15 The advantages of this slow or drop wise co-precipitation method are that the synthesized mixed metal oxides were obtained in nanosize and having high surface area. Previously, we have synthesized the MgO–ZrO2 catalyst by co-precipitation using magnesium nitrate [Mg (NO3)26H2O] and zirconium oxychloride [ZrOCl28H2O] was found to have an excellent catalytic activity for the Knoevenagel condensation reaction, under solvent-free conditions.22 In this article, we have modified the co-precipitation technique with increased quantity of distilled water ten times, than the previous one, stirring speed 5000 RPM, while, it was 400–500 RPM in the previous method and catalyst calcinations also done by gradient heating for 10 h (ESIw). Due to a large quantity of distilled water, we called this method ‘‘ultra-dilution co-precipitation method’’. Catal. Sci. Technol., 2011, 1, 1653–1664

1653

Notably, the surface area of the catalyst is increased from 42.3 to 268.7 m2 g1 and MgO–ZrO2 particles were obtained in nano size (TEM). The prepared MgO–ZrO2 catalyst was characterized by several analytical techniques such as XRD, FT-IR, TG-DTA, nitrogen adsorption, SEM-EDS, TEM and XPS. In continuation of our efforts to study the catalytic activity of heterogeneous catalysts as well as mixed metal oxides,16 the MgO–ZrO2 catalyst was tested for various important organic reactions such as cross-aldol condensation, Cbz–protection of amines, reduction of aromatic nitro compounds and synthesis of 1,5-benzodiazepines.

Experimental All commercial reagents were used as received unless otherwise mentioned. For analytical and preparative thin-layer chromatography, Merck, 0.2 mm and 0.5 mm Kieselgel GF 254 pre-coated were used, respectively. Catalyst preparation

determined the strength of basic sites on catalysts by an indicator method.17 The basic site was found to be stronger than H_ = 26. Here H_ is the acidity function and is defined as a measure of ability of the basic solution to abstract a proton from an acidic solute. Transmission Electron Microscopy (TEM) experiments were performed on a Hitachi 8100 microscope with a Rontec standard EDS detector and digital image acquisition. The scanning electron microscopy (SEM) analysis (FEI, Quanta 200) was carried out to study the surface morphology. The MgO–ZrO2 fine powder was placed on a carbon stub and the images were recorded at 5–15 kV using an LFD detector under low vacuum. XPS measurements were performed on a VSW XPS system with the Class 100 energy analyzer being a part of an experimental setup assembled for surface investigation. The spectra were taken in fixed analyzer transmission mode with the pass energy of 22 eV i.e. FAT 22. The analysis has been performed using the non-monochromatic Al Ka line (photon energy of 1486.3 eV) in order to enable recording of the most intensive Mg 1s XPS peak at about 1303 eV. MgO–ZrO2 fine powder was prepared for XPS by pressing on an In (Indium) plate as a matrix in order to reduce the charging problems and provide a mechanical support. For the energy axis calibration Ag (110) and polycrystalline Au samples (previously cleaned by ion sputtering) were used. The energy was calibrated to the peak position of Ag 3d5/2 (binding energy of 368.22 eV) and Au 4f7/2 (binding energy of 83.96 eV) lines.

In continuation of our interest to explore the utility of the MZ catalyst in organic synthesis, we have successfully prepared the MgO–ZrO2 catalyst, by an ultra dilution method as described below. In a typical experiment, for the preparation of MgO–ZrO2 an appropriate amount of magnesium nitrate [Mg(NO3)2 6H2O] (3.10 g) and zirconium oxychloride [ZrOCl28H2O] (8.11 g) was dissolved together in a 2 L flask with 1 L deionized water. Dilute ammonia solution was added dropwise with vigorous stirring (RPM-5000) until the precipitation was complete (around 6 to 8 h and pH = 10.0). The resultant precipitate was filtered and washed with distilled water till free from chloride ions. The residue was dried for 24 h at 383 K in an oven and the obtained precipitate of metal hydroxides heated in a porcelain crucible progressively to 873 K for 10 hours (ESIw).

The XRD spectrum of MgO–ZrO2 is depicted in Fig. 1. Monoclinic ZrO2 and cubic MgO phases were observed in powder diffraction patterns of MZ. A small shoulder diffraction peak was recognized as a tetragonal phase of ZrO2 at 2y = 301. The XRD pattern shows the presence of both MgO and ZrO2 in the sample.18

Catalyst characterization

Particle size analysis

After calcinations, the MZ catalyst was characterized by various analytical and spectroscopic techniques. The X-ray powder diffraction pattern was obtained using a conventional powder diffractometer (Philips 1050) using graphite monochromatized Cu-Ka radiation operating in Bragg–Brentano (y/2y) geometry. Nitrogen adsorption measurements were carried out at 196 1C using Micromeritics ASAP 2020. The total pore volume was evaluated from the amount of nitrogen adsorbed at the highest relative pressure of 0.99. The pore-size distribution was estimated by applying the BJH method to the desorption isotherm. Before each measurement, the samples were degassed at 4 103 mbar at 200 1C for 10–12 h. The particle size of the catalyst was determined on a computerized inspection system (Galai–Cis–1). Thermogravimetric analysis (TGA) and differential thermal analysis (DTA) under a nitrogen atmosphere were carried out by using Seiko instruments Model-326. The thermal traces under an air (static) atmosphere were recorded employing Mettler Toledo star instruments. The Fourier transform infrared spectrum (FT-IR) of the sample was recorded on a Nicolet–360 FT-IR spectrometer using KBr pellets. We have also

The particle size of MgO–ZrO2 is shown in Fig. 2. The MgO–ZrO2 catalyst was ground to 100 mesh sizes. The particle size is in the range 0.5–0.7 mm.

1654

Catal. Sci. Technol., 2011, 1, 1653–1664

X-Ray diffraction analysis

Fig. 1 XRD spectrum of MgO–ZrO2.

This journal is

c

The Royal Society of Chemistry 2011

Particle size profile of MgO–ZrO2.

Fig. 2

FT-IR spectrum of MgO–ZrO2 The Fourier transform infrared spectrum (FT-IR) of MgO–ZrO2 shows a strong absorption at 470 cm1 due to the Zr–O vibration. The intense bands were observed at 3385 and 1630 cm1, it could be due to hydrated compounds.19 The FT-IR spectrum of MZ in the n(OH) region shows one broad band around 3600–3700 cm1, this band corresponds to –OH stretching vibrations of surface hydroxyl groups.20 The peaks observed at 1190 cm1 and 1440 cm1 could be due to Mg–O interaction21 (Fig. 3). BET surface area and pore size analysis The textural characterization of MgO–ZrO2 was performed by BET surface area, pore volume and average pore diameter measurements (Table 1). N2 adsorption–desorption isotherms of the MgO–ZrO2 sample are shown in Fig. 4. The system corresponds to a type IV nitrogen adsorption isotherm with the characteristic H1 type hysteresis at around

Fig. 3

Table 1

P/P0 = 0.40–0.80. The hysteresis loop formed is due to the capillary condensation within the mesopores and is indicative of well ordered uniform shape and size of mesopores. The sharp increase in adsorption at higher pressures and the one step capillary condensation indicate the presence of large and uniform mesopores respectively. The surface area was 268.7 m2 g1, while in our previous report22 it was only 42.3 m2 g1. It could be due to slow precipitation in a bulk amount of water, with vigorous stirring (5000 RPM) and gradient heating of the hydroxides (ESIw). TG-DTA profile of MgO–ZrO2 The thermal stability of the prepared sample was investigated by a TGA/DTA method. The thermogram obtained for the uncalcined MgO–ZrO2 is presented in Fig. 5. Thermogravimetric analysis (TGA) and differential thermal analysis

FT-IR spectrum of MgO–ZrO2.

Nitrogen physisorption of MgO–ZrO2 BET surface area/ Pore volume/ m2 g1 cm3 g1

Catalyst MgO ZrO2 MgO–ZrO2 (co-precipitation) MgO–ZrO2 (ultradilution) a

Fig. 4 Nitrogen adsorption–desorption isotherm.

Average pore diameter/A˚

26.1 18.1 42.3

0.25 0.14 0.37

42.522 38.322 53.422

268.7

0.22

30.9a

Present work BET measurements.

This journal is

c

The Royal Society of Chemistry 2011

Fig. 5 TG-DTA profile of MgO–ZrO2.

Catal. Sci. Technol., 2011, 1, 1653–1664

1655

(DTA) were applied to the precursor hydroxide to determine the temperature for conversion of the precursors to MgO–ZrO2. Both measurements were carried out from 30 1C to 650 1C at a heating rate of 5 1C min1. The analysis showed that the thermal decomposition consists of two major exothermic peaks in the differential thermal curve indicating that the hydroxides are thermally stable up to nearly 250 1C. The TG profile was characterized by two peaks of weight loss till 514 1C. The first one occurs at 30 1C to 277 1C (18.5% weight loss). The second weight loss occurred between (6.6% weight loss) 277 1C and 514 1C. The DTA profile showed two decompositions till 532 1C. First one occurs at 257 1C and the second decomposition at 532 1C.

Fig. 6

1656

TEM, SEM-EDS analysis Transmission Electron Microscopy (TEM) experiments were performed on a Hitachi 8100 microscope with a Rontec standard EDS detector and digital image acquisition. From TEM and SEM images, it is clear that MgO–ZrO2 particles were obtained in a nano size range and showed uniformsized particles with somewhat spherical morphology with an average size range of 20–35 nm. TEM and SEM images are depicted in Fig. 6a–c. The EDS spectrum of the MgO–ZrO2 catalyst clearly indicates the presence of Mg and Zr metals (Fig. 6d).

(a) TEM images of MgO–ZrO2 at 100 nm and (b) at 50 nm; (c) SEM image of MZ at 1 mm; (d) EDS spectrum of MgO–ZrO2.

Catal. Sci. Technol., 2011, 1, 1653–1664

This journal is

c

The Royal Society of Chemistry 2011

X-Ray photoelectron spectroscopy The survey spectrum of MgO–ZrO2 is shown in Fig. 7. The most intensive XPS and Auger lines are marked by arrows. Besides the main Zr, O and Mg lines (the last being of very small intensity) we also observed In lines (from the support) and also a C 1s line which is expected impurity. The chemical composition of the powder was determined from the characteristic XPS peak intensities of Zr, O and Mg i.e. Zr 3d, O 1s and Mg 1s. In order to improve the sensitivity, the lines were recorded with long acquisition times. As for the sensitivity factors, we use recommended values for the Mg Ka line,23 which should differ from those for the Al Ka line up to 10%. This should give us fair estimation of the chemical surface composition of the sample. The preliminary spectrum analysis shows that all peaks are systematically shifted towards higher binding energies, which we attributed to surface charging. The standard way to determine the energy shift due to charging is from the position of the C 1s peak, which should be at 284.9 eV (according to the NIST database) assuming that it originates from saturated hydrocarbons. The determined peak shift due to charging was 5.1 eV. The XPS peaks of main interest i.e. O 1s, Zr 3d and Mg 1s are given in Fig. 8–10. Zr 3d and Mg 1s can be fitted to a single contribution while O 1s is best fitted to two contributions. The adopted peak model was a pseudo-Voigt profile taken as a product of Gaussian and Lorentzian profiles with the same position and the respective relative intensities 70 and 30 (GL30). The background subtraction has been performed using the approach of Shirley.24 The identification of the contributions is performed using the NIST database available online.25 Zr 3d lines are fitted to two contributions corresponding to 3d5/2 and 3d3/2 lines, respectively. Their intensity ratio is 59.97 : 40.03 which practically coincides with theoretically expected 60 : 40. FWHM of both peaks is 1.85 eV and their positions are 182.1 eV and 184.5 eV, respectively. The reported position of 3d5/2 for ZrO2 is in the range 182–184 eV, and the closest values to ours are reported in references.26 The Mg 1s XPS line (Fig. 9) is fitted to a single contribution having the position of 1303.7 eV (the peak width is 2.2 eV FWHM) which fits well to 1303.9 eV reported for MgO.27,30

Fig. 7

Survey spectrum of ZrO2–MgO powder supported on In plate.

This journal is

c

The Royal Society of Chemistry 2011

Fig. 8 Zr 3d XPS line taken with the energy step of 0.1 eV and acquisition time window of 11 s.

Fig. 9 Mg 1s XPS line taken with the energy step of 0.1 eV and acquisition time window of 22 s.

Fig. 10 O 1s XPS line taken with the energy step of 0.1 eV and acquisition time window of 14 s.

Catal. Sci. Technol., 2011, 1, 1653–1664

1657

As for the O 1s peak (Fig. 10), it was fitted to two contributions with the relative intensities 87.3 : 12.7. The peak positions are 530.0 eV and 532.2 eV while their widths are 2.1 eV. The range of reported positions for O 1s in ZrO2 is 529.9–531.3 eV and the values 530.2 eV28,29 and 529.9 eV30 were reported to be closer to our values. As for the additional contribution, and having in mind the analysis of other peaks, it is reasonable to attribute it to MgO. Indeed, the range of reported O 1s positions for MgO is 530–532.1 eV, and the value closest to our second contribution is reported31 at 532.1 eV. Fig. 11 Influence of catalyst loadings.

Results and discussion After characterization of the MgO–ZrO2 (MZ) catalyst, we have tested its catalytic activity by carrying out several important organic reactions such as cross-aldol condensation, Cbz-protection of amines, catalytic transfer hydrogenation of nitro compounds and synthesis of 1,5-benzodiazepine. It has been observed that MZ gave excellent results for all types of reactions compared to its component oxides. The reactions are described as below. Cross-aldol condensation The cross-aldol condensation is a general method for the formation of a carbon–carbon bond in many classes of carbonyl compounds.32 Cross-aldol condensation of aromatic aldehydes with cyclic ketone is an important synthetic reaction for the preparation of a,a 0 -bis-cycloalkanones. These benzylidene derivatives are important precursors for the synthesis of bioactive pyrimidine derivatives.33 They also play an important role as intermediates of perfumes,34 pharmaceuticals, and agrochemicals. Considering these important applications of cross-aldol products in mind, we have tested the MZ catalyst for the cross-aldol condensation reactions of various aromatic aldehydes with cylcohexanone under solvent-free conditions at room temperature (Scheme 1). In order to study the effect of catalyst loading for crossaldol reaction, we have carried out reaction between benzaldehyde and cyclohexanone under solvent-free conditions. The results are depicted in Fig. 11. It has been observed that 10 wt% of the catalyst is sufficient to catalyze the reaction to afford maximum yield (95%). We did not observe considerable increase in yield for 15 wt% and 20 wt% of the catalyst; however, 5 wt% of the MZ catalyst gives lower yield (55%). After study of this reaction, we have explored the catalytic activity of MZ for some other aldehydes. The result is depicted in Table 2.

Under the solvent free reaction conditions, substituted aromatic aldehydes such as p-methoxy, p-nitrobenzaldehyde, and cinnamaldehyde worked well to give excellent yields of the corresponding products (94–97% yield). We have also tested the reusability of MZ for the model reaction of benzaldehyde with cyclohexanone (Fig. 12). After completion of the reaction monitored by TLC, the catalyst was filtered off, washed with ethyl acetate several times, dried under vacuum at 60 1C for 6 hours and activated at 120 1C for 3 h and used for the next cycle. We observed that the yield of the corresponding product slightly decreased after the sixth cycle. General experimental procedure for cross-aldol condensation To a mixture of cyclohexanone (5 mmol) and aldehyde (10 mmol), was added MgO–ZrO2 (10 wt% with respect to ketone) and reactants were stirred at room temperature for 30 min under solvent-free conditions. The formation of product was monitored by thin layer chromatography. After completion of the reaction, the reaction mixture was dissolved in ethyl acetate and filtered off the catalyst from the reaction mixture and the solvent was concentrated and the product was purified by recrystallization in ethanol. Cbz protection of amines In a wide range of chemical conversions such as amino acid, peptide, glycopeptide, b-lactam, amino glycoside, and nucleoside synthesis, the nucleophilicity and basicity of the amino function can cause problems. The challenge of designing new amino protecting groups that are stable to a wide range of reaction conditions continues to attract a deal of attention.36 The benzyloxycarbonyl (Cbz) protected amines are useful synthetic precursors for various pharmaceuticals and natural products.37 This group is an important functionality for the protection of amines and amine derivatives, since it can be

Scheme 1 MgO–ZrO2 catalyzed cross-aldol condensation under solvent-free conditions.

1658

Catal. Sci. Technol., 2011, 1, 1653–1664

This journal is

c

The Royal Society of Chemistry 2011

Table 2

Cross-aldol condensation reaction of aromatic aldehydes with cyclohexanonea Melting point/1C Isolated yield (%)

Observed

Reported

1

95

116–118

117–11835

2

96

161–162

161–16335

3

94

163–165

164–16535

4

97

176–178

177–17835

No.

Product

a

Reaction conditions—cyclohexanone = 5 mmol, aldehyde = 10 mmol, MgO–ZrO2 (10 wt% with respective of ketone), time = 30 min. Solvent-free.

Fig. 12 Reusability profile of MZ for cross-aldol reaction.

easily removed by catalytic hydrogenation without any side reactions and is stable to basic and most aqueous acidic conditions.38 There are several methods available for the protection of amino groups as N-Cbz derivatives, which include LiHMDS

Scheme 2

This journal is

c

as a base in THF-HMPA (hexamethyl phospharamide) solvent, b-cyclodextrin in aqueous medium, I2 and La(NO3)36H2O under solvent free conditions.39 However, still there is scope to develop new methodology for Cbz protection of amines. The MgO–ZrO2 catalyst was tested for benzyloxycarbonylations of amines under solvent-free conditions at room temperature (Scheme 2). A variety of amines worked well to give the corresponding N-Cbz products in excellent yield (Table 3). This methodology provides a convenient method for the Cbz-protection of a wide range of amines such as aromatic (Table 3, entries 1 and 2), aliphatic (entry 3) and heterocyclic amines (entry 4). We have proposed the following mechanism for the benzyloxycarbonylation of aniline with Cbz chloride (Fig. 13). In first step, the –NH2 group of aniline and Cbz-Cl is adsorbed on the catalyst41 as shown in I. It is well known that functional groups containing electronegative atoms such as N, O, and S are adsorbed on a metal or a Lewis acid site and hydrogen is adsorbed on oxygen of the catalyst.42 Then in the second step electrophilicity of carbonyl carbon of Cbz-Cl is

N-Benzyloxycarbonylation of amines under solvent-free conditions over MgO–ZrO2.

The Royal Society of Chemistry 2011

Catal. Sci. Technol., 2011, 1, 1653–1664

1659

Table 3 N-Benzyloxycarbonylation of amines under solvent-free conditions using the MgO–ZrO2 catalysta Entry

Amines

Product

Isolated yield (%)

94, 91b

1

(10 wt% w.r.t. amine) and the reaction mixture was stirred under solvent-free conditions at room temperature for an appropriate time. After completion of the reaction, the product was extracted in ethyl acetate (3  5 mL). The combined organic layer was washed with brine, dried over anhydrous sodium sulfate and concentrated under reduced pressure to give a crude product which was purified by recrystallisation in ethanol, without any column purification. Reduction of aromatic nitro compounds

2

50c 95 96d

3

84

4

96

a

Reaction conditions amine = 1 mmol, Cbz-Cl = 1.2 mmol, MZ = 10 wt% with respective of amines, solvent-free, room temperature, time = 10 min for all reactions. All compounds are well characterized and reported in the literature.40 b Yield after the fifth cycle. c 5 wt% catalyst used. d 15 wt% catalyst used.

The catalytic transfer hydrogenations of aromatic nitro compounds to the corresponding amines is an important step in the industrial synthesis of dyes, biologically active compounds, pharmaceuticals, rubber chemicals, and photographic and agricultural chemicals.43 A wide range of methods have been developed for this purpose.44 In general for the reduction reactions, which involve hazardous molecular hydrogen or Fe/HCl45or Sn/HCl46 catalytic transfer hydrogenation (CTH) employing hydrogen donors, e.g., propan-2-ol, is harmless, greatly selective, and environment friendly.47 Various methods have been developed for the reduction of nitro compounds such as sodium borohydride/catalyst,48 hydrazine catalyst,49 Cu nanoparticles/ HCOONH4,50 S8/NaHCO3,51 HI,52 and Sm/I2.53 Previously we have explored catalytic transfer hydrogenation reactions over heterogeneous catalysts,54,55 and we herewith report MZ for catalytic transfer hydrogenation of aromatic nitro compounds. We have found that MZ is the best candidate for the catalytic transfer hydrogenation reactions of aromatic nitro compounds to the corresponding amines (Scheme 3). We have used KOH as a promoter and IPA (propan-2-ol or isopropyl alcohol) is a hydrogen source for the reduction reactions. However, in the absence of either IPA or KOH, we have not observed the corresponding product. The results

increased and it generates an intermediate state II, which, finally yields the final product III along with liberation of HCl. The MgO–ZrO2 catalyst participates in all these steps by weakening the chemical bonds of reactants and subsequently lowering the activation energy. Typical experimental procedure The corresponding amine (1 mmol) was added to benzyloxycarbonyl chloride (Cbz-Cl) (1.2 mmol) in the presence of MZ

Scheme 3 Reduction of aromatic nitro compound by using MgO–ZrO2.

Fig. 13 Mechanism of Cbz protection of aniline with benzyloxycarbonyl chloride over MZ.

1660

Catal. Sci. Technol., 2011, 1, 1653–1664

This journal is

c

The Royal Society of Chemistry 2011

Table 4 Catalytic transfer hydrogenations of aromatic nitro compounds in the presence of MgO–ZrO2 to the corresponding aminesa Time/h

Isolated yield (%)

Isolated yield after 5th cycle

1

2

94

91

2

3

96

92

No.

Reactant

Product

Fig. 15 Influence of catalyst wt%.

3

4

94

91

4

4

90

87

a

Reaction conditions: nitrocompound (2 mmol), KOH pellets (2 mmol); catalyst (10 wt% with respect to starting materials); propan-2-ol (5 ml), reflux.

of catalytic transfer hydrogenation reaction over MZ are depicted in Table 4. The effect of reaction time was examined for the reduction of nitrobenzene and it was observed that MZ gives quantitative yield (94%) within 2 hours; however in 3 hours of time, the yield of aniline was not increased further (94%). Therefore, the reaction time 2 h was optimal for the reduction of nitrobenzene to aniline (Fig. 14). The effect of catalyst loading was also examined for the reduction of nitrobenzene. It was observed that 10 wt% catalyst is enough to give excellent yield for the reduction reaction, while further increase in the amount of catalyst such as 15 wt%, 20 wt% did not affect the yield of the product (Fig. 15). The further substrates scope is depicted in Table 4.

Fig. 14 Influence of reaction time on % yield.

This journal is

c

The Royal Society of Chemistry 2011

All aromatic nitro substituted compounds such as –Cl, –CH3 and –OCH3 are compatible under these reaction conditions and no other side products were observed. We have proposed the following possible mechanism for hydrogen transfer reaction of nitroarenes to aromatic amines (Fig. 16). Previously, we have described the mechanism of catalytic transfer hydrogenation over g-Fe2O3.56 During adsorption of propan-2-ol the hydrogen from the –OH gets adsorbed as proton and hydrogen of C–H migrates via hydride transfer to the substrate. Hence the rate of reaction can show dependence on the strength of adsorption of both propan-2-ol and substrate. First nitrobenzene and isopropyl alcohol adsorbed on nano-MgO–ZrO2 I, then reduction of nitrobenzene with IPA as a hydrogen source generates an intermediate II with elimination of an acetone molecule, then intermediate III with elimination of a water molecule and finally aniline V via intermediate IV. General procedure for reduction reaction In a typical CTH reaction, KOH pellets (2 mmol) were dissolved in propan-2-ol (5 mL) to which the substrate (2 mmol) was added along with the catalyst. It was then refluxed for a few hours depending upon the nature of the substrate. After completion of the reaction monitored by thin layer chromatography, the reaction mixture was extracted in ethyl acetate and repeatedly washed with water (5 to 7 times) to remove KOH. The obtained aromatic amines were purified by preparative TLC using ethyl acetate and hexane as eluent. Synthesis of 1,5-benzodiazepine 1,5-Benzodiazepines are generally synthesized by acid catalyzed condensation of o-phenylenediamines with ketones. A large number of catalytic processes are reported for the synthesis of benzodiazepines which include the use of various metal salts, CAN, heteropolyacids, ionic liquids etc.57 1,5-Benzodiazepines are biologically important molecules and are extensively used clinically as analgesic, hypnotic, sedative and antidepressive agents.58 Also, benzodiazepines and their derivatives are a useful functionality of bioactive compounds. They are applicable and are broadly used as anticonvulsant, anti-inflammatory, analgesic, hypnotic, sedative, and antidepressive agents.59 Benzodiazepines are also valuable intermediates for the synthesis of fused ring compounds such as triazolo-, oxadiazolo-, oxazino-, and furano-benzodiazepines.60 Catal. Sci. Technol., 2011, 1, 1653–1664

1661

Fig. 16 Mechanism for reduction of nitroarenes to aromatic amines over MZ.

The feasibility of the catalyzed process was shown by using various substrates. Various ketones such as aliphatic and aromatic gave excellent yield with OPDA. The results are depicted in Table 5. We have studied the reusability of the MZ catalyst for all reactions; we have found that no considerable decrease in yield was observed even after five cycles. Scheme 4 MgO–ZrO2 catalyzed synthesis of 1,5-benzodiazepine by using cyclohexanone and orthophenylene diamine.

We have carried out reaction of orthophenylene diamine (OPDA) with various ketones by using MgO–ZrO2 under solvent-free conditions at room temperature. It has been noted that all ketones such as aliphatic, cyclic and aromatic worked well under solvent-free conditions to obtain the corresponding benzodiazepines in good yield. The reaction of cyclohexanone and orthophenylene diamine (OPDA) is depicted in Scheme 4. The influence of time was examined for the reaction between cyclohexanone and OPDA, it was observed that 1.5 h was sufficient time for the synthesis of 1,5-benzodiazepine in excellent yield. However, at 2.0 h, there is no considerable increase in the yield of the corresponding product was observed (Fig. 17).

Fig. 17 Influence of time for the reaction of cyclohexanone with OPDA.

1662

Catal. Sci. Technol., 2011, 1, 1653–1664

General procedure for the synthesis of 1,5-benzodiazepine In a 10 mL round bottom flask orthophenylene diamine (1 mmol), ketone (2.5 mmol) and 20 wt% catalyst were added. The reaction mixture was stirred at room temperature. The progress of the reaction was monitored by TLC with hexane and ethyl acetate (5 : 1) as eluent. The reactions were completed in 1.5 h. After the completion of the reaction, reaction mixture was extracted with ethyl acetate and compounds were purified by recrystallisation in ethanol. All the products were known compounds and were characterized by FT-IR and 1 H NMR spectroscopic data.61

Conclusions Nano-MgO/ZrO2 was found to catalyze efficiently a variety of organic reactions such as cross-aldol condensation, Cbzprotection of amines, reduction of aromatic nitro compounds, and synthesis of 1,5-benzodiazepine. In cross-aldol condensation reactions, the corresponding products were obtained in excellent yield, under solvent-free conditions. The significant features of this process include high yields, ambient temperature, ease of product isolation and reusability of the catalyst. N-Benzyloxycarbonylation of amines worked well under solvent-free conditions to yield the corresponding N-Cbz products in quantitative yield. Reduction of aromatic nitro compounds to the corresponding amines worked well by using IPA as a hydrogen source and KOH as a promoter. Synthesis of 1,5-benzodiazepine derivatives using MgO–ZrO2 under solvent-free conditions at room-temperature resulted in excellent yield of compounds. We believe that this versatile catalyst can also be useful for other important organic reactions and This journal is

c

The Royal Society of Chemistry 2011

Table 5

Synthesis of 1,5-benzodiazepine derivatives using MgO–ZrO2 under solvent-free conditions at room-temperaturea Melting point/1C Isolated yield (%)

Yield (%) after 5th cycle

Found

Reported

1

97

95

135–136

137–13961

2

95

93

137–138

137–13961

3

92

89

136–137

138–13961

4

93

90

150–151

151–15261

Entry

a

Ketone

Product

Reaction conditions: OPDA (1 mmol), ketone (2.5 mmol), catalyst 20 wt% w.r.t. ketone, time=1.5 h.

has great scope in catalysis technology. Further development and applications of MgO–ZrO2 mixed metal oxide nanoparticles are under progress in our laboratory.

Acknowledgements Manoj Gawande thanks to Foundation of Science and Technology, Portugal for the award of Research Fellowship SFRH/BPD/64934/2009 and financial support.

References 1 S. V. Merzlikin, N. N. Tolkachev, L. E. Briand, T. Strunskus, C. Wall, I. E. Wachs and W. Grunert, Angew. Chem., Int. Ed., 2010, 49, 8037. 2 J. Geserick, T. Froschl, N. Husing, G. Kucerova, M. Makosch, T. Diemant, S. Eckle and R. J. Behm, Dalton Trans., 2011, 40(13), 3269. 3 S. M. Saqer, D. I. Kondarides and X. E. Verykios, Appl. Catal., B, 2011, 103, 275. 4 J. A. Rodriguez and D. Stacchiola, Phys. Chem. Chem. Phys., 2010, 12, 9557. 5 J. B. Park, J. Graciani, J. Evans, D. Stacchiola, S. Ma, P. Liu, A. Nambu, J. F. Sanz, J. Hrbek and J. A. Rodriguez, Proc. Natl. Acad. Sci. U. S. A., 2009, 116, 4975. 6 J. J. Yu, X. P. Wang, L. D. Li, Z. P. Hao, Z. P. Xu and G. Q. (Max) Lue, Adv. Funct. Mater., 2007, 17, 3598; C. Lucarelli, P. Moggi, F. Cavani and M. Devillers, Appl. Catal., A, 2007, 325, 24; L. J. I. Coleman, W. Epling, R. R. Hudgins and E. Croiset, Appl. Catal., A, 2009, 363, 52. 7 H. Cui, M. Zayat and D. Levy, J. Sol–Gel Sci. Technol., 2005, 35, 175; A. Elia, P. Martin Aispuro, N. Quaranta, J. M. MartınMartınez and P. Vazquez, Macromol. Symp., 2011, 301, 136; Y. J. Kim, S. B. Rawal, S. D. Sung and W. I. Lee, Bull. Korean Chem. Soc., 2011, 32, 141. 8 B. M. Reddy, B. Chowdhury and P. G. Smirniotis, Appl. Catal., A, 2001, 211, 19; G. Sankar, C. N. R. Rao and T. Rayment, J. Mater. Chem., 1991, 1, 299.

This journal is

c

The Royal Society of Chemistry 2011

9 A. Tang, H. Yang and X. Zhang, Int. J. Phys. Sci., 2006, 1, 101; V. V. Zyryanov, Inorg. Mater, 2003, 39, 1163. 10 S. Ajaikumar and A. Pandurangan, Appl. Catal., A, 2009, 357, 184; W. C. Sheets, E. S. Stampler, H. Kabbour, M. I. Bertoni, L. Cario, T. O. Mason, T. J. Marks and K. R. Poeppelmeier, Inorg. Chem., 2007, 46, 10741. 11 D. Jiang, L. Su, L. Ma, N. Yao, X. Xu, H. Tang and X. Li, Appl. Surf. Sci., 2010, 256, 3216; B. M. Reddy and I. Ganesh, J. Mol. Catal. A: Chem., 2001, 169, 207. 12 G. K. Pradhan and K. M. Parida, Int. J. Eng. Sci. Technol., 2010, 2, 53. 13 M. Zhang, T. An, X. Hu, C. Wang, G. Sheng and J. Fu, Appl. Catal., A, 2004, 260, 215. 14 M. Zhang, G. Sheng, J. Fu, T. An, X. Wang and X. Hu, Mater. Lett., 2005, 59, 3641. 15 H. Abimanyu, B. S. Ahn, C. Soo Kim and K. S. Yoo, Ind. Eng. Chem. Res., 2007, 46, 7936. 16 S. K. Mohapatra, S. U. Sonavane, R. V. Jayaram and P. Selvam, Org. Lett., 2002, 4, 4297; S. N. Koyande, R. G. Jaiswal and R. V. Jayaram, Ind. Eng. Chem. Res., 1998, 37, 908; M. B. Gawande, S. S. Deshpande, S. U. Sonavane and R. V. Jayaram, J. Mol. Catal. A: Chem., 2005, 241, 151; D. M. Nagrik, D. M. Ambhore and M. B. Gawande, Int. J. Chem., 2010, 2, 98; S. J. Singh and R. V. Jayaram, Tetrahedron Lett., 2008, 49, 4249; M. B. Gawande, S. S. Deshpande, J. R. Satam and R. V. Jayaram, Catal. Commun., 2007, 8, 576. 17 J.-I. Take, N. Kikuchi and Y. Yoneda, J. Catal., 1971, 21, 164. 18 L. Zhao, J. Zhao, M. Luo, G. Liu, J. Song and Y. Zhang, Catal. Commun., 2005, 6, 617; F. Li, Y. Wang, W. Xue and X. Zhao, J. Chem. Technol. Biotechnol., 2007, 82, 209–213. 19 L. A. Perez-Maqueda and E. Matijevi, J. Mater. Res., 1997, 12, 3286. 20 K. Hadjiivanov and J.-C. Lavalley, Catal. Commun., 2001, 2, 129. 21 M. H. Lee and D. G. Park, Bull. Korean Chem. Soc., 2003, 24, 1437. 22 M. B. Gawande and R. V. Jayaram, Catal. Commun., 2006, 7, 931. 23 C. D. Wagner, L. E. Davis, M. W. Zeller, J. A. Taylor, R. M. Raymond and L. H. Gale, SIA Surf. Interface Anal., 1981, 3, 211. 24 D. P. Shirley, Phys. Rev. B, 1972, 5, 4709. 25 http://srdata.nist.gov/xps/Default.aspx.

Catal. Sci. Technol., 2011, 1, 1653–1664

1663

26 A. E. Hughes and B. A. Sexton, J. Electron Spectrosc. Relat. Phenom., 1990, 50, c15; V. I. Nefedov, D. Gati, B. F. Dzhurinskii, N. P. Sergushin and Y. V. Salyn, Zh. Neorg. Khim., 1975, 20, 2307; G. Carta, N. Habra, G. Rossetto, P. Zanella, M. Casarin, D. Barreca, C. Maragno and E. Tondello, Surf. Coating Technol., 2007, 201, 9289; D. D. Sarma and C. N. R. Rao, J. Electron Spectrosc. Relat. Phenom., 1980, 20, 25. 27 H. Seyama and M. Soma, J. Chem. Soc. Faraday Trans., 1984, I 80, 237. 28 V. I. Nefedov, D. Gati, B. F. Dzhurinskii, N. P. Sergushin and Y. V. Salyn, Zh. Neorg. Khim., 1975, 20, 2307. 29 G. Carta, N. E. Habra, G. Rossetto, P. Zanella, M. Casarin, D. Barreca, C. Maragno and E. Tondello, Surf. Coatings Technol., 2007, 201, 9289. 30 H. Seyama and M. Soma, J. Chem. Soc. Faraday Trans., 1984, I 80, 237. 31 D. D. Sarma and C. N. R. Rao, J. Electron Spectrosc. Relat. Phenom., 1980, 20, 25. 32 M. B. Smith and J. March, March’s advanced organic chemistry: reactions, mechanisms and structure, John Wiley & Sons, New York, 2001; R. D. Norcross and I. Paterson, Chem. Rev., 1995, 95, 2041; B. M. Trost, I. FlemingComprehensive Organic Synthesis: 9-Volume Set, Pergamon, Oxford, 1991, Vol. 2, Parts 1.4–1.7. 33 J. Deli, T. Lonard, D. Szabo and A. Foldesi, Pharmazie, 1984, 39, 539. 34 M. Ogawa, Y. Ishii, T. Nakano and S. Irifune, Jpn. Kohai Tokkyo JP 63192446 A2, 1988 (Chem. Abstr., 1988, 63, 238034). 35 J. J. Shrikhande, M. B. Gawande and R. V. Jayaram, Catal. Commun., 2008, 9, 1010. 36 G. Theodoridis, Tetrahedron Lett., 1998, 39, 9365. 37 E. A. Papageorgiou, M. J. Gaunt, J.-Q. Yu and J. B. Spencer, Organic Lett., 2000, 2, 1049. 38 D. B. Berkowitz and M. L. Pedersen, J. Org. Chem., 1994, 59, 5476; P. E. Maligres, I. Houpis, K. Rossen, A. Molinga, J. Sager, V. Upadhyay, K. M. Wells, R. A. Reamer, J. E. Lynch, D. Askin, R. P. Volante and P. J. Reider, Tetrahedron, 1997, 32, 10893. 39 J. N. Hernandez and V. S. Martin, J. Org. Chem., 2004, 69, 3590; V. Pavan Kumar, M. S. Reddy, K. Narender and K. R. Rao, Tetrahedron Lett., 2006, 47, 6393; R. Varala, R. Enugala and S. R. Adapa, J. Iran. Chem. Soc., 2007, 4, 370; K. C. Mahesh, M. Narasimhulu, T. S. Reddy and N. S. Venkateswarlu, Tetrahedron Lett., 2007, 48, 55. 40 M. B. Gawande, V. Polshettiwar, R. S. Varma and R. V. Jayaram, Tetrahedron Lett., 2007, 48, 8170. 41 S. Saravanamurugan, M. Palanichamy, B. Arabindoo and V. Murugesan, Catal. Commun., 2005, 6, 399; A. Solhy, W. Amer, M. Karkouri, R. Tahir, A. E. Bouari, A. Fihri, M. Bousmina and M. Zahouily, J. Mol. Catal. A: Chem., 2011, 336, 8. 42 K. Tanabe and W. F. Holderich, Appl. Catal. A, 1999, 181, 399. 43 G. W. Kabalka and R. S. Varma, In Comprehensive Organic Synthesis, ed. B. M. Trost and I. Fleming, Pergamon, Oxford, UK, 1991, Vol. 8, pp. 363. 44 R. C. Larock, Comprehensive Organic Transformations: A Guide to Functional Group Preparation, Wiley-VCH, New York, 2nd edn, 1999, p. 823.

1664

Catal. Sci. Technol., 2011, 1, 1653–1664

45 C. A. Merlic, S. Motamed and B. Quinn, J. Org. Chem., 1995, 60, 3365. 46 K. M. Doxsee, M. Fiegel, K. D. Stewart, J. W. Canary, C. B. Knobler and D. J. Cram, J. Am. Chem. Soc., 1987, 109, 3098. 47 G. V. Smith and F. Notheisz, Heterogeneous Catalysis in Organic Chemistry, Academic, New York, 1999, p. 71. 48 A. Rahman and S. B. Jonnalagadda, Catal. Lett., 2008, 123, 264. 49 Q. Shi, R. Lu, L. Lu, X. Fu and D. Zhao, Adv. Synth. Catal., 2007, 349, 1877. 50 A. Saha and B. Ranu, J. Org. Chem., 2008, 73, 6867. 51 M. A. McLaughlin and D. M. Barnes, Tetrahedron Lett., 2006, 47, 9095. 52 J. S. D. Kumar, M. M. Ho and T. Toyokuni, Tetrahedron Lett., 2001, 42, 5601. 53 B. K. Banik, C. Mukhopadhyay, M. S. Venkaraman and F. F. Becker, Tetrahedron Lett., 1998, 39, 7243. 54 S. U. Sonavane and R. V. Jayaram, Synth. Commun., 2003, 33, 843; S. U. Sonavane and R. V. Jayaram, Synlett, 2004, 146; P. Selvam, S. U. Sonvane and R. V. Jayaram, Adv. Synth. Catal., 2004, 346, 542. 55 A. S. Kulkarni and R. V. Jayaram, J. Mol. Catal. A: Chem., 2004, 223, 107; A. S. Kulkarni and R. V. Jayaram, Appl. Catal. A., 2003, 252, 225. 56 S. U. Sonavane, M. B. Gawande, S. S. Deshpande, A. Venkataraman and R. V. Jayaram, Catal. Commun., 2007, 8, 180. 57 S. D. Sharma, P. Gogoi and D. Konwar, Green Chem., QJ;2007, 9, 153; M. S. Balakrishna and B. Kaboudin, Tetrahedron Lett., 2001, 42, 1127; B. Kaboudin and K. Navace, Heterocycles, 2001, 55, 1443; M. Pozarentzi, J. S. Stephanatou and C. A. Tsoleridis, Tetrahedron Lett., 2002, 43, 1755; B. P. Bandgar, S. V. Bettigeri and N. S. Joshi, Synth. Commun., 2004, 34, 1447; J. S. Yadav, B. V. S. Reddy, N. Lingaiah and P. S. Saiprasad, Synthesis, 2004, 901; J. S. Yadav, B. V. S. Reddy, S. Praveenkumar and K. Nagaiah, Synthesis, 2005, 480; M. A. Pasha and V. P. Jayashankara, Heterocycles, 2006, 68, 1017; M. Curini, F. Epifano, M. C. Marcotullio and O. Rosati, Tetrahedron Lett., 2001, 42, 3193; S. K. De and R. A. Gibbs, Tetrahedron Lett., 2005, 46, 1811. 58 H. Schutz, Benzodiazepines, Springer, Heidelberg, 1982, Vol. 2, pp. 240–275; L. O. Randall and B. Kappel, In Benzodiazepines Synthesis of Benzodiazepine Derivatives, ed. S. Garattini, E. Mussini and L. O. Randall, Raven Press, New York, 1973, p. 27, and references therein. 59 H. Schutz, Benzodiazepines, Springer, Heidelberg, 1982; L. O. Randall and B. Kamel, In Benzodiazepines, S. Garattini, E. Mussini and L. O. Randall, Raven Press, New York, 1973, p. 27, and references cited therein. 60 M. Essaber, A. Baouid, A. Hasnaoui, A. Benharref and J.-P. Lavergne, Synth. Commun., 1998, 28, 4097; A. M. El-Sayed, H. Abdel-Ghany and A. M. M. El-Saghier, Synth. Commun., 1999, 29, 3561; K. V. V. Reddy, P. S. Rao and D. Ashok, Synth. Commun., 2000, 30, 1825. 61 R. Varala, R. Enugala, S. Nuvula and S. R. Adapa, Synlett, 2006, 1009.

This journal is

c

The Royal Society of Chemistry 2011