Electrical properties of thin zirconium and hafnium oxide high-k gate

0 downloads 0 Views 530KB Size Report
EG&G 5206 two-phase lock-in analyzer to measure the con- ductance, and an HP 54501A digital oscilloscope to record the complete conductance transient.
Electrical properties of thin zirconium and hafnium oxide high-k gate dielectrics grown by atomic layer deposition from cyclopentadienyl and ozone precursors S. Dueñas,a兲 H. Castán, H. Garcia, A. Gómez, and L. Bailón Departamento de Electricidad y Electrónica, E. T. S. I. Telecomunicación, Universidad de Valladolid, 47011 Valladolid, Spain

K. Kukli Institute of Physics, Department of Materials Science, University of Tartu, 51010 Tartu, Estonia and Department of Chemistry, University of Helsinki, 00014 Helsinki, Finland

J. Niinistö, M. Ritala, and M. Leskelä Department of Chemistry, University of Helsinki, 00014 Helsinki, Finland

共Received 28 May 2008; accepted 22 September 2008; published 9 February 2009兲 ZrO2 and reference HfO2 films grown by atomic layer deposition from metal cyclopentadienyls and ozone as precursors to thicknesses ranging from 3.6 to 13.1 nm on etched silicon showed electrical characteristics adequate to high-k dielectrics. The best results in terms of low interface state densities were obtained when 共CpMe兲2ZrMe2 precursor was used, with Cp denoting the cyclopentadienyl group 共C5H5兲, and Me the methyl group 共CH3兲. The ZrO2 films grown from 共CpMe兲2Zr共OMe兲Me possessed nearly an order of magnitude higher trap state densities. Similar dependence on the precursor chemistry was observed upon recording the flatband voltage time transients. The flatband voltage transients, originating from phonon-assisted tunneling between localized states at oxide silicon interface, were the lowest in HfO2 films grown from 共CpMe兲2Hf共OMe兲Me. The leakage current densities were also lower in the HfO2 films, compared to ZrO2. On the other hand, interfacial trap state densities in HfO2 based capacitors remained higher than those measured in the case of ZrO2 films. Process-dependent qualities of the capacitors have been described. At the same time, the current conduction mechanisms in all films were essentially bulk driven, not affected noticeably by the interfacial barriers. © 2009 American Vacuum Society. 关DOI: 10.1116/1.3025865兴

I. INTRODUCTION ZrO2 and HfO2 have gained considerable attention in the microelectronic industry in order to replace SiO2 as capacitor dielectric material,1 at first because of their high permittivity, but also due to large band gap, related high breakdown field, and sufficient thermodynamic stability on Si. Although the interfacial stability of HfO2 on Si tends to be superior to that of ZrO2,2 ZrO2 is still an intriguing material due to its greater ability to form higher-permittivity metastable crystallographic polymorphs. Atomic layer deposition 共ALD兲 of ZrO2 and HfO2 films has been realized using different precursors, most often or traditionally from chlorides,3–5 but also from alternative, e.g., organometallic cyclopentadienyl-based precursors.6–11 Good-quality ZrO2 and HfO2 films can be grown using ALD processes established for 共CpMe兲2ZrMe2,9,11 共CpMe兲2Zr共OMe兲Me,9,11 共CpMe兲2Hf共OMe兲Me,9,10 and O3 as precursors. 共CpMe兲2ZrMe2 may allow better stability of the growth rate against temperature parametrization,11 whereas the 共CpMe兲2Hf共OMe兲Me tended to allow relatively higher growth rates11 and, possibly, stronger contribution from cubic/tetragonal phases in the films grown.10 At the same time, also lower leakage was achieved in the ZrO2 grown a兲

Electronic mail: [email protected]

389

J. Vac. Sci. Technol. B 27„1…, Jan/Feb 2009

from 共CpMe兲2Zr共OMe兲Me.9 The lowest leakage currents have still been characteristic of HfO2 films.9 All these precursors have demonstrated comparable abilities to provide conformal growth over three-dimensional substrates suited to the development of nanoelectronic devices.9,10 In order to further evaluate the potential electrical stability of the films grown in such processes likely exhibiting characteristic advantages and drawbacks, more detailed studies are required. In this work, we have investigated the defect densities and their effect to the capacitive properties and conduction mechanisms of metal-oxide-semiconductor 共MOS兲 structures with ZrO2 and, for comparison, some HfO2 layers atomic layer deposited by using the precursors mentioned above. The electrical characterization techniques used were capacitance-voltage 共C-V兲, deep-level transient spectroscopy 共DLTS兲 to obtain the interfacial state density values, conductance transients 共G-t兲 to obtain the disordered-induced gap states 共DIGS兲 densities, current-voltage 共I-V兲, and constantcapacitance flatband voltage transients 共VFB-t兲. II. EXPERIMENT A. Sample preparation

The measured samples were high-k dielectric based MOS structures. The metal oxide films were grown on HF-etched 1071-1023/2009/27„1…/389/5/$25.00

©2009 American Vacuum Society

389

390

Dueñas et al.: Electrical properties of thin zirconium oxide

TABLE I. Growth parameters and thickness of the atomic layer deposited ZrO2 and HfO2 films. Cp denotes the cyclopentadienyl group 共C5H5兲, Me denotes the methyl group 共CH3兲.

Precursor

Cycles at Tgrowth 共at 350 ° C兲

Thickness by XRR 共nm兲

100 200 300 100 200 300 150 200

3.6 8.1 13.1 3.9 8.0 11.9 5.0 8.3

共CpMe兲2ZrMe2 共CpMe兲2ZrMe2 共CpMe兲2ZrMe2 共CpMe兲2Zr共OMe兲Me 共CpMe兲2Zr共OMe兲Me 共CpMe兲2Zr共OMe兲Me 共CpMe兲2Hf共OMe兲Me 共CpMe兲2Hf共OMe兲Me

390

ductance, and an HP 54501A digital oscilloscope to record the complete conductance transient. The I-V curves were measured with a Keithley 6517A programmable electrometer in the stair sweep voltage mode while the voltage step used was 5 mV. Finally, to obtain the flatband voltage transients we have implemented a feedback system that varies the applied gate voltage accordingly to keep constant the flatband capacitance value. The capacitance is measured by using a Boonton 72B capacimeter, and an electrometer Keithley 6517A is used to read the capacimeter analog output as well as to send the data to the computer. The modular source Agilent N6700 working with the N6761A module provides the bias voltage. III. RESULTS AND DISCUSSION

p-type silicon substrates by ALD in a hot-wall flow-type reactor F120.12 The metal precursors, amounts of growth cycles and growth temperatures are listed in Table I. The growth temperatures were chosen considering the optimum temperature range for a particular precursor applied. The cycle times used were 1-2-2-2 s for the sequence metal precursor pulse-purge-O3 pulse-purge. The thicknesses of the films, also shown in Table I, were evaluated from x-ray reflection patterns. The electrical measurements were carried out on Al/ ZrO2 / p-Si共100兲 / Al or Al/ HfO2 / p-Si共100兲 / Al capacitors. Aluminum dot electrodes with an area of 0.204 mm2 were e-beam evaporated on top of the dielectric layers through a shadow mask. To form nearly Ohmic contacts to silicon substrates, the back sides of the wafers were etched in HF and metallized by evaporating a 100 nm thick Al layer. B. Measurement procedure

In order to record the electrical parameters at several temperatures varying between 77 K and room temperature, the samples were first cooled in darkness from room temperature to 77 K at zero bias in an Oxford DM1710 cryostat. An Oxford ITC 502 controller was used to monitor the temperature during the measurements. The C-V measurements were carried out with the assistance of a Boonton 72B capacitance meter and a Keithley 617 programmable electrometer. The capacimeter makes measurements of shunt capacitance by applying a 1 MHz and 15 mV level ac signal test. Voltage bias consists of 50 mV steps. The capacitance measurements are made 10 s after the bias-voltage step is applied in order to prevent transient instabilities in the capacitance values. Interfacial state densities were obtained by saturating pulse DLTS. The bias voltage was chosen for each sample so that the capacitor was just at the limit between depletion and weak inversion, and a 10 ms wide pulse high enough to drive the capacitors into accumulation was applied in order to fill all interface traps. Information on the traps was obtained by analyzing the capacitance transient that results as the traps empty, i.e., return to equilibrium. The experimental setup of the conductance transient technique consist of an HP 33120A arbitrary wave-form generator to apply the bias pulses, an EG&G 5206 two-phase lock-in analyzer to measure the conJ. Vac. Sci. Technol. B, Vol. 27, No. 1, Jan/Feb 2009

A. Structure and composition of the films

Structural studies have indicated earlier that ZrO2 films grown from 共CpMe兲2Zr共OMe兲Me contained only metastable tetragonal or cubic polymorph.9 In the ZrO2 films grown from 共CpMe兲2ZrMe2 and HfO2 grown from 共CpMe兲2Hf共OMe兲Me, also monoclinic polymorphs became apparent when the ZrO2 films reached a thickness of 12 nm and HfO2 films 8 nm.9 The films thinner than 4 – 5 nm remained amorphous. The crystallized films consisted of dense homogeneous grains, although with distinct grain boundaries. Approximately 0.8– 1.5 nm thick interfacial layer was formed between the film and substrate. The interfacial layer is probably silicon oxide, formed due to the strong oxidizing capability of ozone used as the oxygen precursor. Elastic recoil detection analysis has earlier verified the stoichiometry of HfO2 grown from 共CpMe兲2Hf共OMe兲Me and O3, while the concentration of residual carbon and hydrogen remained lower than 0.1 at. %.10 Rutherford backscattering spectroscopy studies have earlier been carried out on ZrO2, demonstrating low levels of carbon residuals 共below the detection limit, ⬃1 at. %兲.11 Hydrogen content could not be analyzed. However, the oxygen to zirconium atomic ratio could reach 2.06–2.07 in the films grown from 共CpMe兲2Zr共OMe兲Me at 300 ° C and in the films grown from 共CpMe兲2ZrMe2 at 350 ° C,11 referring to the possible presence of hydroxyl groups or carbonates, slightly increasing the relative content of oxygen. B. Electrical characterization results

Normalized 1 MHz C-V curves measured at 77 K for ZrO2 and HfO2 film-based MOS devices are shown in Fig. 1. C-V measurements have also been carried out at room temperature, but the higher leakage currents yield more distorted and confusing curves than those obtained at low temperatures. Since the flatband voltage 共VFB兲 value results mainly from the difference in work function values between the Al electrode and Si substrate 共⌽ms ⬃ −0.5 V兲 and the presence of fixed charges, flatband voltage shift is related to the presence of charge in the dielectric films. It is apparent that when 共CpMe兲2ZrMe2 precursor is used, flatband voltage displacements are lower than in the case of 共CpMe兲2Zr共OMe兲Me and

391

Dueñas et al.: Electrical properties of thin zirconium oxide

391

FIG. 1. Normalized 1 MHz C-V curves measured at 77 K for ZrO2 and HfO2 film-based MOS devices.

共CpMe兲2Hf共OMe兲Me precursors. In the last case, we can also observe that hafnium oxide based samples exhibit less flatband voltage displacements than zirconium oxide based samples. On the other hand, the thinnest films show considerable amount of hysteresis in comparison to thicker samples. Finally, the 3.6 nm thick sample, processed by using 共CpMe兲2ZrMe2, exhibited a flatband voltage displacement around 1 V less than the other samples, so it seems that the 共CpMe兲2ZrMe2 precursor leads to better quality thin films. This last result must be taken by caution due that it has been only observed for one sample. From the flatband voltage shift of C-V curves, values between 1.77⫻ 1012 C cm−2 and 7.01⫻ 1012 cm−2 of the fixed oxide charge densities are estimated. DLTS measurements 共Fig. 2兲 indicated that HfO2 films possessed higher interfacial state densities 共Dit兲 than ZrO2 samples. Also, ZrO2 films grown from the 共CpMe兲2ZrMe2 precursor had lower interface trap densities than the films grown from

FIG. 3. Current-electric field dependency fitting following the Poole-Frenkel model: at different temperatures corresponding to an 8.3 nm thick hafnium oxide based MOS sample 共a兲, and at room temperature corresponding to several hafnium oxide and zirconium oxide based MOS samples 共b兲.

FIG. 2. Interfacial state density distributions obtained by DLTS for ZrO2 and HfO2 film-based MOS devices.

共CpMe兲2Zr共OMe兲Me. For both HfO2 and ZrO2, Dit increases with film thickness. In good agreement with C-V measurements, DLTS results indicate that the best quality interface corresponds to the 3.6 nm thick sample processed by using 共CpMe兲2ZrMe2. The conductance transients recorded were as small as ⌬G / ␻ ⬍ 1 ⫻ 10−12 ⍀−1 Hz−1 at temperatures between 200 and 300 K, and undetectable for our experimental setup at temperatures below 200 K, corresponding to DIGS densities lower than 1 ⫻ 1010 cm−2 eV−1. Prebreakdown current densities were lower in HfO2 films, compared to ZrO2. Current-voltage characteristics of all the samples were well fitted according to the Poole-Frenkel 共PF兲 currents 共Fig. 3兲, indicating that the main conduction mechanism is bulk related.13 Figure 3共a兲 shows the plot of I / E 共in logarithmic scale兲 against E1/2 at several temperatures, corresponding to the 8.3 nm thick hafnium oxide based MOS sample. The PF field-lowering coefficient values, ␤PF, are

JVST B - Microelectronics and Nanometer Structures

392

Dueñas et al.: Electrical properties of thin zirconium oxide

392

FIG. 4. Normalized flatband transients measured at room temperature corresponding to several hafnium oxide and zirconium oxide based MOS samples.

about 共1.4– 1.5兲 ⫻ 10−5 eV m1/2 V−1/2. The theoretical value of ␤PF parameter obtained from the dielectric constant of HfO2 layer at optical frequencies 共about 3.6兲 is 4 ⫻ 10−5 eV m1/2 V−1/2, so the experimental and theoretical values do not completely agree. The good fit of the PooleFrenkel plots can indicate that this difference is related to the physical structure of the films, especially to the existence of an interfacial layer. In Fig. 3共b兲 the PF fits at room temperature corresponding to all samples are depicted. When the 共CpMe兲2M共OMe兲Me 共M = Zr, Hf兲 precursors are used, ␤PF values of about 1.4⫻ 10−5 eV m1/2 V−1/2 are obtained. However, the values of ␤PF are lower 关around 共1.1– 1.3兲 ⫻ 10−5 eV m1/2 V−1/2兴 in the cases of 共CpMe兲2ZrMe2 precursor. Flatband voltage transients recorded at different temperatures provide valuable information about phonon-assisted tunneling mechanisms.14–16 These transients are recorded under conditions without external stress, and so they are originated by phonon-assisted tunneling between localized states, phonons producing the ionization of traps existing in the bandgap of the insulator. Figure 4 shows normalized flatband voltage transients measured at room temperature for the hafnium oxide and zirconium oxide based MOS samples. Transient amplitudes clearly depend on the precursor and the dielectric film. In fact, the transient amplitudes of Al/ ZrO2 / p-Si samples fabricated by using the 共CpMe兲2Zr共OMe兲Me precursor are greater than those obtained when the 共CpMe兲2ZrMe2 precursor is used. Also, flatband voltage transients of Al/ HfO2 / p-Si samples exhibit lower amplitude than those corresponding to Al/ ZrO2 / p-Si samples, in good agreement with the current-voltage behavior. As it has been shown elsewhere,14 the amplitude of flatband voltage transients also depends on temperature. Indeed, their magnitude follows an Arrhenius plot that provides the activation energy of the soft-optical phonons involved in the tunneling mechanism. As it is shown in Fig. 5, activation energy values of about 135– 140 meV are obtained. FourierJ. Vac. Sci. Technol. B, Vol. 27, No. 1, Jan/Feb 2009

FIG. 5. Flatband transients measured at different temperatures, and the Arrhenius plot corresponding to a 3.6 nm thick zirconium oxide based MOS sample 共a兲, and to an 8.3 nm thick hafnium oxide based MOS sample 共b兲.

transform infrared measurements could give straightforward evidence that such mechanism occurs indeed. One can follow systematic differences between the films grown from different precursors, especially in terms of interface state densities, Dit 共Fig. 2兲. The ZrO2 based capacitors were less defective in terms of Dit, compared to HfO2, and, within the ZrO2 serial, 共CpMe兲2ZrMe2 occurred more advantageous compared to 共CpMe兲2Zr共OMe兲Me. Also the flatband transients have been weaker in the films grown from 共CpMe兲2ZrMe2. The chemical purity, i.e., the residual contamination of ZrO2 has not been lower compared to HfO2, but rather slightly excessive oxygen has earlier been considered. Therefore, the electronic defect density and stability might rather be connected to the crystallographic phase composition, at least partially. Indeed, under the deposition conditions applied, stoichiometric stable monoclinic polymorph tended to appear at somewhat lower thicknesses in ZrO2 deposited from 共CpMe兲2ZrMe2, compared to the films grown from 共CpMe兲2Zr共OMe兲Me.9 It is thus possible that the crystallographic phase heterogeneity may not always result in greater density of electronic defects affecting the capacitive

393

Dueñas et al.: Electrical properties of thin zirconium oxide

behavior of MOS devices, provided that only stable stoichiometric phases can be formed at early stages of growth. This, however, does not explain the even greater density of defects observed in HfO2-based MOS structures. Besides, the Dit increases with film thickness in general and thus with crystallographic phase heterogeneity within each series grown using particular growth chemistry 共Fig. 2兲. Nevertheless, although the behavior of Dit and the extent of flatband voltage transients cannot yet be fully explained on the basis of film purity and crystallinity, the electronic behavior recorded carries the features evidently characteristic of the process applied, including precursor chemistry and deposition temperature. IV. CONCLUSIONS The electrical characterization of ALD ZrO2 and HfO2 films as deposited by using cyclopentadienyl based precursors 共CpMe兲2Zr共OMe兲Me, 共CpMe兲2ZrMe2, and 共CpMe兲2Hf共OMe兲Me, with O3, has demonstrated the suitability of these precursors for the fabrication of high-k dielectric materials. In terms of interface trap densities, ZrO2 films grown to thickness lower than 4 nm using 共CpMe兲2ZrMe2 occurred most promising, showing Dit values 共8 – 9兲 ⫻ 1010 cm−2 eV−1, whereas in the films grown from 共CpMe兲2Zr共OMe兲Me the Dit values exceeded 共4 – 5兲 ⫻ 1011 cm−2 eV−1. In HfO2 films, at the same time, the Dit values reached 1 ⫻ 1012 cm−2 eV−1 and higher. Flatband voltage transients, i.e., instabilities of C-V curves, were also weaker in ZrO2 films grown from 共CpMe兲2ZrMe2, compared to the films grown from 共CpMe兲2Zr共OMe兲Me. The flatband transients were even weaker in HfO2 films, compared to the ZrO2 films. Also the prebreakdown current densities were lower in HfO2, indicating, expectably, better insulating properties compared to ZrO2 despite the higher interfacial trap

JVST B - Microelectronics and Nanometer Structures

393

densities. The electrical quality of the high-k films has thus been rather strongly dependent on the material deposited as well as the precursor chemistry applied. In all the films, however, the currents were driven by the bulk properties of the films, rather than interfaces between electrodes and oxide films, as revealed by the Poole-Frenkel characteristics. ACKNOWLEDGMENTS The study was partially supported by the local government 共Junta de Castilla y León兲 under Grant No. VA018A06, and by the Spanish TEC2005 under Grant No. 05101/MIC. The authors wish to thank M. Putkonen for depositing part of the thin film samples. 1

G. D. Wilk, R. M. Wallace, and J. M. Anthony, J. Appl. Phys. 89, 5243 共2001兲. 2 M. Gutowski, J. E. Jaffe, C. L. Liu, M. Stoker, R. I. Hegde, R. S. Rai, and P. J. Tobin, Appl. Phys. Lett. 80, 1897 共2002兲. 3 M. Ritala and M. Leskelä, Appl. Surf. Sci. 75, 333 共1994兲. 4 M. Copel, M. Gribelyuk, and E. Gusev, Appl. Phys. Lett. 76, 436 共2000兲. 5 J. Aarik, A. Aidla, H. Mändar, T. Uustare, and V. Sammelselg,Thin Solid Films 408, 97 共2002兲. 6 M. Putkonen and L. Niinistö, J. Mater. Chem. 11, 3141 共2001兲. 7 M. Putkonen, J. Niinistö, K. Kukli, T. Sajavaara, M. Karppinen, H. Yamauchi, and L. Niinistö, Chem. Vap. Deposition 9, 207 共2003兲. 8 J. Niinistö, M. Putkonen, L. Niinistö, K. Kukli, M. Ritala, and M. Leskelä, J. Appl. Phys. 95, 84 共2004兲. 9 K. Kukli et al., Microelectron. Eng. 84, 2010 共2007兲. 10 J. Niinistö, M. Putkonen, L. Niinistö, F. Song, P. Williams, P. N. Heys, and R. Odedra, Chem. Mater. 19, 3319 共2007兲. 11 J. Niinistö et al., J. Mater. Chem. 18, 3385 共2008兲. 12 T. Suntola, Thin Solid Films 216, 84 共1992兲. 13 J. Frenkel, Phys. Rev. 54, 647 共1938兲. 14 S. Dueñas, H. Castán, H. García, L. Bailón, K. Kukli, T. Hatanpää, M. Ritala, and M. Leskelä, Microelectron. Eng. 47, 653 共2007兲. 15 S. Dueñas et al., J. Electrochem. Soc. 154, G207 共2007兲. 16 S. Dueñas, H. Castán, H. García, A. Gómez, L. Bailón, M. ToledanoLuque, I. Mártil, and G. González-Díaz, Semicond. Sci. Technol. 22, 1344 共2007兲.